Unsymmetrical tertiary-aliphatic azoalkanes

ABSTRACT

Unsymmetrical azo compounds (R&#34;) 3  C--N=N--R&#39; where (R&#34;) 3  C-- is tert.-aliphatic and R&#39; is --C(R 1 )(R 2 )(Z) or ##STR1## e.g., 1-t-butylazo-1-chlorocyclohexane, their use as vinyl polymerization initiators and polyester resin curing agents, and methods for preparing same from t-aliphatic hydrazones and t-aliphatic α-halo-substituted azoalkanes.

RELATED APPLICATIONS

This application is a continuation-in-part of copending application Ser. No. 149,041 filed june 1, 1971, (now abandoned) which is a division of application Ser. No. 725,180 filed Apr. 29, 1968 (now abandoned), which is a continuation-in-part of application Ser. No. 616,158 filed Feb. 15, 1967 (now abandoned).

BACKGROUND OF THE INVENTION

This invention relates to unsymmetrical azo compounds, unsymmetrical hydrazo compounds, processes for preparing these compounds and processes utilizing these compounds, which azo and hydrazo compounds are characterized by having a tertiary carbon atom joined to one of the azo or hydrazo nitrogens.

Symmetrical azo compounds having a tert-carbon atom joined to each azo nitrogen are known:

E. Farenhorst and E. C. Kooyman, Rec. Trav. Chim. 72,993 (1953).

S. F. Nelson and P. D. Barlett, J. Am. Chem. Soc. 88, 137, 143 (1966).

Unsymmetrical azo compounds where a tert-carbon atom is joined to one azo nitrogen are known. Illustrative compounds of this type, none coming within the scope of the invention are given in:

M. C. Chaco and N. Rabjohn, J. Org. Chem. 27, 2765 (1962).

D. C. Iffland, L. Salisbury, and W. R. Schafer, J. Am. Chem. Soc. 83, 747 (1961).

D. Y. Curtin and J. A. Ursprung, J. Org. Chem. 21, 1221 (1956).

C. G. Overberger and A. V. DiGiulio, J. Am. Chem. Soc. 80, 6562 (1958); ibid 81, 2154 (1959).

H. Wieland, et al, Ann. 514, 145 (1934).

The above compounds are in general difficult to prepare, or are so stable that they are not useful as free radical generators or as blowing agents for plastic foams.

2, 2'-AZOBISISOBUTYRONITRILE IS COMMERCIALLY AVAILABLE. This compound has the structure ##STR2## It has many shortcomings. It is a toxic solid. Moreover, the decomposition residue is a highly toxic solid. Thus, it presents a toxic dusting problem when used in commercial operations and extreme precautions are required in its handling. It is not used in many applications for which it is suited because other areas at the manufacturing site cannot tolerate even the remote chance of exposure to such toxic dust. This is especially true when manufacturing goods for the food and drug packaging industries and many other goods for the household consumer. It cannot be used as a blowing agent for the great majority of the plastic foam market due to the high levels of the toxic residue left in the foamed product. It is insoluble in petroleum hydrocarbon solvents and possesses very low or limited solubility in most of the organic common solvents such as aromatic hydrocarbons, dioxane, alcohol, ether and carbon tetrachloride. This insoluble nature eliminates its use for many applications for which it would otherwise be suitable. It presents problems of metering, incorporation, mixing, dispersing, etc. and necessitates the use of a solvent that in many cases is not ideally suited for the particular application.

The new compositions of the present invention eliminate these problems. Most of the new compositions are liquids and are soluble in petroleum hydrocarbon and most of the other common organic solvents. Thus, no dusting, metering, incorporating, mixing, and dispersing problems are encountered in using these new compositions. Also the new compositions and their decomposition residues have chemical structures that suggest that they are, for the most part, significantly less toxic. Preliminary toxicological studies on the new compositions made in Examples I and IV, set out later, and the decomposition residue of the Example I product indicate that they are significantly less toxic than IXA and its decomposition residue. The less toxic nature of the new compositions coupled with their liquid and high solubility properties allows them to be used in many applications where IXA cannot be used.

Unsymmetrical tert-carbon containing hydrazo compounds are known. Illustrative literature showing the prior art types of these compounds is presented:

Thiele, B. 28, 2600.

Angeli, Rome Atti Accad Tincei 26 I, 95 (1917).

Thiele and Strange, Ann 283, 33 (1894). D. Neighbors et al., J. Am. Chem. Soc. 44, 1557 (1922).

BRIEF SUMMARY OF THE INVENTION

1. Unsymmetrical azo compounds (R")₃ C--N=N--R' (I) where (R")₃ C--and--R' are different and where:

1. each R" is separately selected from a lower alkyl (about 1-13 carbons), aralkyl (generally phenalkyl of about 7-12 carbons, normally phenalkyl of 7-9 carbons and preferably phenalkyl of 7-8 carbons), or phenyl (about 6-14 carbons) radical, and not more than one phenyl can be present; and

2. R' is ##STR3## or --R₁₂ --N=N--C(R")₃ ; where a. R₁ and R₂ are separately selected from lower aliphatic (about 1- 20 carbons, normally alkyl of 1-13 carbons or phenalkyl of 7-12 carbons and more commonly alkyl of 1-6 carbons or phenalkyl of 7-9 carbons) or cycloaliphatic (normally mono-, bi- or tri- cycloalkyl of 3-12 carbons or 5-6 membered heterocyclic wherein the hetero atom is O, S or N and more commonly cycloalkyl of 3-6 carbons) radicals and together can form an alkylene biradical (about 2-30 carbons, more commonly 2-16 carbons and preferably 4-7 carbons), and R₂ can also be phenyl (6-14 carbons) or a substituted phenyl;

b. R₃ and R₄ are hydrogen, lower aliphatic (preferably alkyl of 1-4 carbons), or cycloaliphatic (preferably cycloalkyl of 3-6 carbons) radicals and together can form an alkylene biradical (commonly 2-16 carbons and preferably 2-7 carbons);

c. R₅ is a lower aliphatic (normally alkyl of 1-13 carbons and preferably alkyl of 1-4 carbons), cycloaliphatic (preferably cycloalkyl of 3-6 carbons) or aromatic (usually hydrocarbon aryl of 6-14 carbons, more commonly 6-10 carbons and preferably phenyl or alkyl-substituted phenyl of 6-8 carbons) radical;

d. R₆ is a lower alkyl radical (normally 1-13 carbons and preferably 1-4 carbons);

e. R₇ and R₈ are separately selected from hydrogen or lower alkyl (normally 1-13 carbons and preferably 1-4 carbons radicals;

f. R₆ and R₇ together can form an alkylene biradical (2-30 carbons, normally 2-16 carbons and preferably 2-7 carbons);

g. Z' is a zero, mono-, or di-valent remainder of a heterocyclic ring;

(h) Z is a radical: --CN, --C(=O)NH₂, --C(=O)OR₆, --C(=NH)NH₂, --C(=NH)OR₆, --C(=NOH)NH₂, --Cl, --Br, --OC(=O)H, --OC(=O)R₅, --OC(=O)OR₅, --OC(=O)OOR, --SC(=O)R₅, --SC(=S)R₅, --SC(=O)OR₅, --SC(=S)OR₅, --OR₅, --SR₅, --N₃, --SCN, --OCN, --OOR, --OOC(=O)R₅, --OOH, --OH, --R₅, --N(R₁₀)₂ (preferably --NHR₅), --NHN(R₅)₂ (preferably --NHNHR₅), --NHNHC(=O)OR₆, --NO₂, --NO₃, --C.tbd.CR₁₀, ##STR4## (preferably where R₁₀ is R₅), ##STR5## (preferably ##STR6## i. R₁₂ is a biradical: --C(=O)N(R₃)R₁₃ N(R₃)C(=O)--, --C(=O)R₁₃ C(=O)-- , ##STR7## j. Y" is a biradical: --S--S--, --NHNH--, --X"C(=X")R₁₃ C(=X")X"--, --X"C(=X")OR₁₃ OC(=X")X"--, --X"--R₁₃ --X"--, --OOC(=O)R₁₃ C(=O)OO--, ##STR8## k. R₁₃ is an aliphatic, cycloaliphatic, or aromatic biradical; l. X" is oxygen or sulfur;

m. R₁₀ is hydrogen, lower aliphatic, cycloaliphatic, or aromatic;

n. R₁₄ and R₁₅ are --CN, --NO₂, --C(=O)OR₁₀, --C(=O)R₁₀, ##STR9## or -NH₂ ; o. R₁₄ and R₁₅ can together form the biradicals:

--C(=O)R₁₃ C(=O)--, --C(=O)OR₁₃ OC(=O)--,

--c(=o)n(r₆)r₁₃ n(r₆)c(=o)--, ##STR10## p. R has the same definition as (R")₃ C-- but need not be same in any given compound.

2. Novel hydrazo compounds ##STR11## where: a. R" is a lower alkyl, aralkyl or phenyl radical and not more than one phenyl is present; and

b. R₃ and R₄ are hydrogen, lower aliphatic or cycloaliphatic radicals and together may form an alkylene biradical.

3. First process: Preparation of cyanoazo compounds.

A. General Procedure for All Ketones

1. Reacting R--NH--NH₂ and R₁ C(=O)R₂ in the presence of an inert solvent while removing the water produced substantially continuously during the reaction to form (A) R--NH--N=C(R₁) (R₂);

2. reacting ((A) with hydrogen cyanide at a temperature from about 10°to 80°C to form (B) R--NH--NH--C(R₁) (R₂) (CN); and

3. oxidizing (B) to form the desired azo product (C) R--N=N--C(R₁) (R₂) (CN);

where:

a. R is the radical (R")₃ C with R" being a lower alkyl, aralkyl or phenyl radical and not more than one phenyl is present; and

b. R₁ and R₂ are lower aliphatic or cycloaliphatic radicals and together may form an alkylene biradical.

B. General Procedure for water soluble and partially soluble ketones.

Reacting the R-NHNH₂ acid salt with MCN and R₁ --C(O)--R₂ in water to form above and oxidizing to form the corresponding azo product.

4. Second process: Preparation of α-haloazo compounds.

Reacting (A) and halogen (Cl₂ or Br₂) to form the α-haloazo product R--N=N--C(R₁) (R₂) (X) (P) where:

a. R is the radical (R")₃ C--with R" being a lower alkyl, aralkyl or phenyl radical and not more than one phenyl is present;

b. R₁ and R₂ are lower aliphatic or cycloaliphatic radicals and together may form an alkylene biradical, and R₁ may also be phenyl or substituted phenyl; and

c. X is chlorine or bromine.

5. Third process: Preparation of α-substituted-azo compounds.

Reacting R--N=N--C(R₁) (R₂) (X) and MY, MY", or MY"H or (MY"H, YH, HY"H in the presence of a base) to form the α-substituted-azo product (Q) R--N=N--C(R₁) (R₂) (Y) or [R--N=N--C(R₁) (R₂)--]₂ Y"

where: R, R₁, R₂, and X are defined as above and

a. M is an alkali or alkaline earth metal;

b. Y is one of the following radicals: --CN, --OC(=O)H, --OC(=O)R₅, --OC(=O)OR₅, --SC(=O)R₅, --SC(=O)OR₅, --SC(=S) OR₅, --OR₅, --SR₅, --N₃, --SCN, --OCN, --OOR, --OOC(=O)R₅, -- OOH, --OH, --R₅, ##STR12## c. R, R₁, R₂, R₃, R₄, R₅, R₆, R₁₀, and Y" are as defined hereinbefore;

d. R'₁₄ and R'₁₅ are --C(=O)OR₆, --CN, -C(=O)R₅, or --NO₂ ;

e. R₁₃ is an aliphatic, cycloaliphatic or aromatic biradical and R'₁₄ and R'₁₅ are as defined hereinbefore; and

f. X" is oxygen or sulfur.

Compounds prepared by this third process wherein Y is ##STR13## are readily converted to the novel azo compounds wherein Z is ##STR14## by conventional processes well known to the art.

6. Fourth process: Preparation of amidazo compounds.

Reacting R--N=N--C(O)OR₉, and HN(R₃) (R₄), or HN(R₃)R₁₃ N(R₃)H, to form the azo products R-N=N--C(O)N(R₃)(R₄), or R--N=N--C(O)N(R₃)R₁₃ N(R₃)C(O)--N=N -R, and R₉ OH where:

a. R is the radical (R")₃ C-- with R" being a lower alkyl, aralkyl or phenyl radical and not more than one phenyl is present;

b. R₃ and R₄ are hydrogen, lower aliphatic or cycloaliphatic radicals and together may form an alkylene biradical;

c. R₉ is a lower alkyl radical; and

d. R₁₃ is an aliphatic, cycloaliphatic or aromatic biradical.

7. Fifth process: Preparation of azoacyl compounds.

1. Reacting R--NH--NH₂ and R₅ C(=O)X, or XC(=O)R₁₃ C(=O)X, in a liquid solvent which does not contain active hydrogen radicals and in the presence of an alkaline material to form

G. (r')₃ c--nh--nh--c(=o)r₅ , or

(G¹) (R")₃ C--NHNHC(=O)R₁₃ C(=O)NHNHC(R")₃

2. oxidizing G or G¹ form the azo products

H. (r")₃ c--n=n--c(=o)r₅, or

H¹ (r")₃ cn=n--c(=o)r₁₃ c(=o)n=nc(r")₃

where:

(a. R₅ is a lower aliphatic, cycloaliphatic or aromatic radical;

b. X is a chloro, bromo or iodo radical; and

c. R₁₃ is an aliphatic, cycloaliphatic, or aromatic biradical.

8. Sixth process: Preparation of heterosubstituted azo compounds.

1. Reacting R-NH-NH₂ ##STR15## in a liquid solvent which does not contain active hydrogen radicals and in the presence of an alkaline material to form

K. ##STR16##

2. oxidizing K to form the azo product

L. ##STR17## where: a. R is the radical (R")₃ C--with R" being a lower alkyl or phenyl radical and not more than one phenyl is present;

b. Z' is a zero, mono, or divalent remainder of a heterocyclic ring; and

c. X is chloro, bromo or iodo.

9. Seventh process: Preparation of amidohydrazo compounds.

Reacting (R")₃ C--NH--NH₂. HX' with H₂ NC(=O)N(R₁₁)₂ in an aqueous medium at a temperature between about 50° -100°C to form (R")₃ C--NH--NH--C(=O)-N(R₁₁)₂ where:

a. R₁₁ is hydrogen or lower alkyl radical; and

b. X' is chloro, bromo, iodo, SO=₄ or HSO--₄.

10. Eighth process: Another preparation of amidohydrazo compounds.

Reacting (R")₃ --C--NH--NH₂ with M'CNO in an aqueous medium to form (R")₃ C--NH--NH--C(=O)--N(R₁₁)₂ where:

a. R₁₁ is hydrogen; and

b. M' is a metal or hydrogen radical.

DESCRIPTION OF THE INVENTIONS 1. Novel Azo Compounds

The scope of the novel azo compounds of the invention has been set out in the summary in connection with Formula I.

The tertiary group joined to one of the azo nitrogens is illustrated by the following ##STR18## where ##STR19## indicates a lower alkyl radical, i.e., one having 1 to about 13 carbons and normally being acyclic alkyl of 1-8 or cycloalkyl (mono, bi or tri) or 3-12 carbons. Tertiary group (a) is preferably a tert-butyl or tert-amyl radical ##STR20## may include one or more hydrocarbon substitutes such as tolyl and xylyl or may contain 2 or 3 condensed rings as in naphthyl or phenanthryl preferably indicates a group such as benzyl or phenethyl. For convenience the tertiary group is designated (R")₃ C-. The compounds having the tri ##STR21## -C group are a preferred sub-genus. Two or more of the R"s can also join to form a cyclo-, bicyclo- or tricyclo- radical (preferably cycloalkyl) of 3-12 carbons.

The group R' joined to the other azo nitrogen is one of the radicals listed in the definition of Formula I. These radicals may be designated as t-aliphatic radicals (but not identical to (R")₃ C-- in any specific compound), α-substituted tertiary aliphatic radicals, acyl radicals, amido radicals, olefins having the unsaturation adjacent a secondary carbon atom, and nitrogen containing heteroradical, where aliphatic includes cycloaliphatic. The terms aliphatic radical and cycloaliphatic radical are used in their normal chemical meaning ---- the non-hydrocarbon substituents must not interfere with the preparation reaction(s). In general a lower aliphatic radical will have 1 -- about 20 carbon atoms and the cycloaliphatic will have 1 or 2 condensed rings and may have hydrocarbon substituents in the ring. Commonly these will be cyclopentyl and cyclohexyl rings.

R₁ and R₂, R₃ and R₄, R₆ and R₇, and R₇ and R₈ together may form an alkylene biradical. The biradicals may contain 2-30 or more carbon atoms; more commonly 2-16 carbon atoms; and preferably 2-7 carbons.

R₁ and R₂ (and the aryl groups in R") can contain substituents such as lower alkoxy (lower indicating about 1-4 carbons), aryloxy (preferably phenoxy), lower alkyl, hydroxy, carboxy, lower alkoxycarbonyl, lower alkylcarbonyloxy, phenylcarbonyloxy, halogen (preferably chlorine or bromine) or cyano.

The term aromatic radical is used in its normal chemical sense of a benzene ring or condensed benezene rings which may be substituted by one or more individual groups or a non-aromatic ring. The preferred aromatic radical is a phenyl group.

The group ##STR22## represents a nitrogen containing heterocyclic radical where [Z'] represents the atoms or groups of atoms which are present in the ring and also the substituents thereon.

The above definitions are broad and intentionally so because the defined R's and Z's appearing in the radical definitions of the azo compounds of Formula I do not affect the general utility of the compounds or the ability to make the compound by the processes set forth herein. Numerous compounds coming with Formula I are set out in the working examples.

Examples of R" radicals are methyl, ethyl, propyl, i-propyl, butyl, i-butyl, sec-butyl, t-butyl, amyl, i-amyl, sec-amyl, t-amyl, hexyl, t-hexyl, heptyl, octyl, t-octyl, cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cyclooctyl, cyclododecyl, perhydronaphthyl, adamantyl, bicyclo [2. 2. 1] heptyl, benzyl, α-cumyl, 2-(β-naphthyl)ethyl, phenyl, o, m and p-tolyl, naphthyl, triethylphenyl, phenanthryl, p-t-butylphenyl and neopentyl.

Examples of (R")₃ C radicals are t-butyl, t-amyl, t-cumyl, t-adamantyl, t-(1-phenyl)cyclopentyl, t-(1-phenyl)cyclohexyl, t-(2-methyl)bicyclo [2.2.1]heptyl, t-(2-methyl)bicyclo [2.2.2]-octyl, t-(1-phenyl)cyclopropyl, t-octyl, t-dodecyl, t-(α-methyl-α-ethyl)benzyl, t-(α, α-diethyl)benzyl.

Examples of R₁ radicals are methyl, ethyl, propyl, i-propyl, butyl, i-butyl, sec-butyl, t-butyl, amyl, i-amyl, sec-amyl, t-amyl, hexyl, t-hexyl, neopentyl, 2-methoxy-2-methylpropyl, n-octyl, t-octyl, cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cyclooctyl, cyclododecyl, perhydronaphthyl, adamantyl, bicyclo-[2.2.1]heptyl, benzyl, α-cumyl, α-methyl-α-ethylbenzyl, α, α-diethylbenzyl, α-ethyl-α-propylbenzyl, 1-phenylcyclohexyl, 3, 3, 5-trimethylcyclohexyl, 4-t-butylcyclohexyl, methylcyclohexyl, trimethylcyclopentyl and 4-i-propylcyclohexyl.

Examples of R₂ radicals are the same as the R₁ radicals plus phenyl, o, m and p-toluyl, naphthyl, triethylphenyl, phenanthryl, p-t-butylphenyl, m and p-methoxyphenyl, o, m and p-bromo (or chloro)phenyl, xylyl, m-cyclopropylphenyl, p-cyclohexylphenyl and i-propylphenyl.

Examples where R₁ and R₂ are joined together are 1,1,3,3-tetramethyl- 2-oxo-propylene, propylene, butylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, nonamethylene, undecamethylene and 1,2 or 3-methylpentamethylene.

Examples of Substituents in R₁ and R₂ are ethenyl, allyl, hexenyl, cyclopentenyl, methylcyclohexenyl, ethynyl, propynyl, hexynyl, cyclooctynyl, methoxy, ethoxy, propoxy, hexoxy, isopentoxy, methylcyclopentoxy, cyclohexoxy, phenoxy, naphthoxy, chlorophenoxy, dimethylphenoxy, ethylphenoxy, cyclohexylphenoxy, acetoxy, propionoxy, isohexanoyloxy, cyclohexanecarbonyloxy, benzoyloxy, naphthoyloxy, chlorobenzoyloxy, methylbenzoyloxy, methylnaphthoyloxy, methoxycarbonyl, ethoxycarbonyl, butoxycarbonyl, cyclohexoxycarbonyl, phenoxycarbonyl, naphthoxycarbonyl, chlorophenoxycarbonyl, methylphenoxycarbonyl, methylbiphenyloxycarbonyl, acetyl, propionyl, valeroyl, cyclohexanecarbonyl, benzoyl, naphthoyl, chlorobenzoyl, methylbenzoyl, methylnaphthoyl, cyano, chlorine, bromine, iodine, fluorine, hydroxy, and, when X is not --OH, carboxy.

A preferred embodiment includes compounds I where Z is CL, --OH or --OC(=O)OR₅. In addition to compounds exemplified hereinafter, some representative α-substituted azos of the invention include the following (for brevity, all those listed are α-chloroazos or α-hydroxyazos, it being understood that other Z groups above could be substituted therefor as the α-substituent group):

1. 2-t-cumylazo-2-hydroxypropane

2. 2-t-butylazo-2-hydroxy-tetradecane

3. 1-t-butylazo-1-cyclopropyl-1-hydroxyethane

4. 1-t-adamantylazo-1-cyclohexyl-1-hydroxyethane

5. 1- [t-(α-methyl-α-ethyl-nonyl)azo]-1-cyclododecyl-1-hydroxy-ethane

6. 1- [t-(α, α-dimethyl-β-phenylethyl)azo]-1-cyclopentyl-1 -hydroxyethane

7. 1- [t-(1, 1-dimethyl-7-phenylheptyl)azo]-1-cyclooctyl-1 -hydroxyethane

8. 1- [t-(p-t-butylcumyl)azo]-1-norborn-2-yl-1-hydroxyethane

9. 1- [t-(1-(phenanthr-2-yl)-1-methylethyl)azo]-1-adamant-2-yl- 1-hydroxyethane

10. 2- [t-(decalylazo)]-2-hydroxy-1-phenylpropane

11. 3- [t-(1-methylcyclopentyl)azo]-3-hydroxy-1-naphth-2-ylbutane

12. 2- [t-(α-methyl-α-ethylpropyl)azo]-2-hydroxy-1 -(p-t-butyl)phenylpropane

13. 1- [t-(α, α-diethylpropyl)azo]-1-hydroxy-1-phenylethane

14. 2-t-(amylazo)-2-hydroxy-5-phenylpentane

15. 1- [t-(α, α-dimethylpentyl)azo]-1-hydroxy-1-phenanthr-2-ylethane

16. 1- [t-(α-methyl-α-cyclopropylethyl)azo]-1-hydroxy-1-naphth- 2-ylethane

17. 2- [t-(α,α-dimethyl-β-phenylethyl)azo]-2-hydroxybutane

18. 2- [t-(1-methylcyclododecyl)azo]-2-hydroxypropane

19. 1- [t-(α-methyl-α-cyclododecylethyl)azo]-1-hydroxycyclobutane

20. 2- [t-(α-methyl-α-cyclooctylethyl)azo]-2-hydroxy(2.2.2-bicyclooctane

21. 1- [t-(α-methyl-α-(norborn-2-yl)ethyl)azo]-1-hydroxycyclododecane

22. 1- [t-(α-methyl-α-(2.2.2-bicyclooct-2-yl)azo]-1-hydroxycyclooctane

23. 1- [t-(α-t-adamantyl-α-methylethyl)azo]-1-hydroxycyclodecane

24. 2- [t-(1, 1-dimethyl-4-phenylbutyl)azo]-2-hydroxynorbornane

25. 2- [t-(α-methyl-α-naphth-2-ylethyl)azo]-2-hydroxyadamantane

26. 2- [t-(1-methylcyclopropyl)azo]-2-hydroxy-4-methyl-4 -phenoxypentane

27. 2- [t-(2-methylnorborn-2-yl)azo]-2,4 -dihydroxy-4-methylpentane

28. 2- [t-(α,α-dimethyl-γ-naphth-2-ylpropyl)azo]-2,5-dihydroxypentane

29. Phenyl 5- [t-(α-methyl-α-naphth-2-ylethyl)azo]-5 -hydroxyhexanoate

30. 1- [t-(α-methyl-α-(p-methylphenyl)ethyl)azo]-1-hydroxy-1 -(p-chlorophenyl)ethane

31. 1- [t-(1-methylcyclohexyl)azo]-1-hydroxy-1-(m-bromophenyl)-ethane

32. 1- [t-(1-methylcyclooctyl)azo]-1-hydroxy-1-(p-fluorophenyl) ethane

33. 1- [t-(butyl)azo]-1-hydroxy-1-(p-iodophenyl)propane

34. 3- [t-(butyl)azo]-3-hydroxy-1-benzoyloxybutane

35. 1- [t-(amyl)azo]-1-hydroxy-1-(p-cyanophenyl)ethane

36. 2- [t-(1,1,3,3-tetramethylbutyl)azo]-2-hydroxy-5-aminopentane

37. 1- [t-(1,1,3-trimethylbutyl)azo]-1-hydroxy-1-cyclobutylethane

38. 2- [t-(α,α-dimethylbenzyl)azo]-2-hydroxytetralin

39. 4- [t-(α, α-diisobutylethyl)azo]-4-hydroxy-2,7-dimethylheptane

40. 2- [t-(1,1,3,3-tetramethylbutyl)azo]-2-hydroxy-3,3-dimethylbutane

41. 2- [t-(α,α-dimethyl-p-chlorobenzyl)azo]-2-hydroxy-4,4 -dimethylpentane

42. 2- [t-(α,α-dimethyl-m-bromobenzyl)azo]-2-hydroxydecane

43. 2- [t-(α, α-dimethyl-p-cyanobenzyl)azo]-2-hydroxyindane

44. 1- [t-(2-methyltetral-2-yl)azo]-1-hydroxy-1-(fur-2-yl)-ethane

45. 1- [t-(α,α-diisobutylethyl)azo]-1-hydroxy-1-(tetrahydrofur- 2-yl)ethane

46. 1- [t-(α,α,β,β-tetramethylpropyl)azo]-1-hydroxy-1 -(pyrid-4-yl)ethane

47. 1- [t-(α,α-dibenzylethyl)azo]-1-hydroxy-1-(thiophen- 2-yl)ethane

48. 1- [t-(2-methylindan-2-yl)azo]-1-hydroxy-1-(anthracen- 9-yl)ethane

49. 1- [t-(α,α-dicyclopropylethyl)azo]-1-hydroxy-1-(pyrid- 2-yl)ethane

50. 2- [t-(α,α-dicyclohexylethyl)azo]-2-hydroxy-3-methylbutane

51. 2-t-cumylazo-2-bromopropane

52. 2-t-butylazo-2-chlorotetradecane

53. 1-t-butylazo-1-cyclopropyl-1-bromoethane

54. 1-t-adamantylazo-1-cyclohexyl-1-chloroethane

55. 1- [t-(α-methyl-α-ethylnonyl)azo]-1-cyclododecyl-1 -chloroethane

56. 1- [t-(α,α-dimethyl-β-phenylethyl)azo]-1-cyclopentyl-1 -chloroethane

57. 1- [t-(1,1-dimethyl-7-phenylheptyl)azo]-1-cyclooctyl-1 -chloroethane

58. 1- [t-(p-t-butylcumyl)azo]-1-norborn-2-yl-1-chloroethane

59. 1- [t-(1-(phenanthr-2-yl)-1-methylethyl)azo]-1-adamant-2-yl- 1-chloroethane

60. 2- [t-(decalylazo)]-2-chloro-1-phenylpropane

61. 3- [t-(1-methylcyclopentyl)azo]-3-chloro-1-naphth-2-yl-butane

62. 2- [t-(α-methyl-α-ethylpropyl)azo]-2-chloro-1-(p-t-butyl)-phenylpropane

63. 1- [t-(α,α-diethylpropyl)azo]-1-chloro-1-phenylethane

64. 2-t-(amylazo)-2-chloro-5-phenylpentane

65. 1- [t-(α,α-dimethypentyl)azo]-1-chloro-1-phenanthr-2-yl-ethane

66. 1- [t-(α-methyl-α-cyclopropylethyl)azo]-1-chloro-1-naphth- 2-ylethane

67. 2- [t-(α,α-dimethyl-β-phenylethyl)azo]-2-chlorobutane

68. 2- [t-(1-methylcyclododecyl)azo]-2-chloropropane

69. 1- [t-(α-methyl-α-cyclododecylethyl)azo]-1-chlorocyclobutane

70. 2- [t-(α-methyl-α-cyclooctylethyl)azo]-2-chloro-(2.2.2 -bicyclooctane)

71. 1- [t-(α-methyl-α-(norborn-2-yl)ethyl)azo]-1-chlorocyclododecane

72 1- [t-(α-methyl-α-(2.2.2-bicyclooct-2-yl)azo]-1-chlorocyclooctane

73. 1- [t-(α-t-adamantyl-α-methylethyl)azo]-1-chlorocyclodecane

74. 2- [t-(1,1-dimethyl-4-phenylbutyl)azo]-2-chloronorbornane

75. 2- [t-(α-methyl-α-naphth-2-ylethyl)azo]-2-chloroadamantane

76. 2- [t-(1-methylcyclopropyl)azo]-2-chloro-4-methyl-4 -phenoxypentane

77. 2- [t-(2-methylnorborn-2-yl)azo]-2-chloro-4-hydroxy-4 -methylpentane

78. 2- [t-(α,α-dimethyl-γ-naphth-2-ylpropyl)azo]-2-chloro- 5-hydroxypentane

79. Phenyl 5- [t-(α-methyl-α-naphth-2-ylethyl)azo]-5-chlorohexanoate

80. 1- [t-(α-methyl-α-(p-methyphenyl)ethyl)azo]-1-chloro-1 -(p-chlorophenyl)ethane

81. 1- [t-(1-methylcyclohexyl)azo]-1-chloro-1-(m-bromophenyl)- ethane

82. 1- [t-(1-methylcyclooctyl)azo]-1-chloro-1-(p-fluorophenyl)-ethane

83. 1- [t-(butyl)azo]-1-chloro-1-(p-iodophenyl)propane

84. 3- [t-(butyl)azo]-3-chloro-1-benzoyloxybutane

85. 1- [t-(amyl)azo]-1-chloro-1-(p-cyanophenyl)ethane

86. 2- [t-(1,1,3,3-tetramethylbutyl)azo]-2-chloro-5-aminopentane

87. 1- [t-(1,1,3-trimethylbutyl)azo]-1-chloro-1-cyclobutylethane

88. 2- [t-(α,α-dimethylbenzyl)azo]-2-chlorotetralin

89. 4- [t-(α,α-diisobutylethyl)azo]-4-chloro-2,7,dimethylheptane

90. 2- [t-(1,1,3,3-tetramethylbutyl)azo]-2-chloro-3,3-dimethylbutane

91. 2- [t-(α,α-dimethyl-p-chlorobenzyl)azo]-2-chloro-4,4-dimethylpentane

92. 2- [t-(α,α-dimethyl-m-bromobenzyl)azo]-2-chlorodecane

93. 2- [t-(α,α-dimethyl-p-cyanobenzyl)azo]-2-chloroindane

94. 1- [t-(2-methyltetral-2-yl)azo]-1-chloro-1-(fur-2-yl)ethane

95. 1- [t-(α,α-diisobutylethyl)azo]-1-chloro-1-(tetrahydrofur- 2-yl)ethane

96. 1- [t-(α,α,β,β-tetramethylpropyl)azo]-1-chloro-1-(pyrid- 4-yl)ethane

97. 1- [t-(α,α-dibenzylethyl)azo]-1-chloro-1-(thiophen-2-yl)-ethane

98. 1- [t-(2-methylindan-2-yl)azo]-1-chloro-1-(anthracen-9-yl)-ethane

99. 1- [t-(α,α-dicyclopropylethyl)azo]-1-chloro-1-(pyrid-2-yl)-ethane

100. 2- [2-(α,α-dicyclohexylethyl)azo]-2-chloro-3-methylbutane

Utility

These new compositions are free radical generators, polymerization initiators, curing agents for polyester resins, initiators for free radical initiated chemical reactions, blowing agents for producing foamed polymers and plastics, and selective oxidizing agents.

It has been observed that these new compositions are initiators for the polymerization or copolymerization of unsaturated monomers such as alkenes, vinyl halides, vinyl esters, vinylidene halides and alkenyl aromatics.

Illustrative polymerizable monomers are ethylene, vinyl chloride, vinylidene chloride, vinyl acetate, vinylpyridine, vinylpyrrolidone, vinylcarbazole, butadiene, isoprene, acrylonitrile, acrylic acid, acrylic acid esters, methacrylic acid, methacrylic acid esters, styrene, chlorostyrene and metyl styrenes.

It has also been observed that certain of these novel compounds i.e. Examples I b, and IV b, are especially advantageous initiators in the high pressure polymerization of ethylene.

The new compositions of Formula I, in which R' is one of the defined radicals, excluding --C(ZR₁ R₂), also possess very reactive azo linkages. These azo compounds can undergo Diels-Alder reactions, allylic hydrogen additions, and free radical additions at the nitrogen-nitrogen double bond as well as thermal decomposition to give free radicals and gas. They are therefore valuable chemical intermediates and reactants.

Specific illustrations of utility are given in the working examples. Other illustrations are found in copending Ser. No. 453,446 filed Mar. 21, 1974 (now abandoned in favor of Ser. No. 548,946 filed Feb. 11, 1975) of Ronald E. MacLeay et al entitled "Process for Preparing Foamed Structures".

Preparation

The new azo compositions of the present invention are easily prepared from hydrazines containing one of the defined tertiary groups R, as shown in the following working examples. The tert-alkylhydrazines have been very difficult and tedious to prepare and have been laboratory curiosities prior to the filing of U.S. patent application Ser. No. 409,306, filed 11/5/64 (now abandoned in favor of Ser. No. 684,651 filed 1/17/67 (now abandoned), Ser. No. 684,651 filed 11/21/67 (now U.S. Pat. No. 3,746,760 issued (7/17/73), Ser. No. 684,652 filed 11/21/67 (now U.S. Pat. No. 3,657,324 issued 4/18/72) and Ser. No. 684,653 (now U.S. Pat. No. 3,522,233 issued 7/28/70) by C. S. Sheppard and L. E. Korczykowski and of common assignment. The new process described in this patent application Ser. No. 409,306 produces tertiary alkylhydrazines in a simple and very economical manner and it is ideally suited for commercial production this process comprises reacting an N-monohalomonosubstituted urea, ##STR23## with an alkaline material in the presence of a compound affording an active hydrogen in an organic solvent; under conditions such that said alkaline material is present at all times in an amount at least adequate to said urea; where X and X' are different and are selected from the class consisting of halogen and hydrogen; and R_(m) is selected from the class consisting of alkyl, aryl, aralkyl, cycloalkyl, heteroalkyl, carbalkoxy and carbaryloxy. Thus, the methods of producing the new compositions of the present invention are economically feasible and are not difficult to carry out on a commercial scale.

Six novel processes for preparation of compounds coming with Formula I are described separately hereinafter.

A process for preparing olefinically substituted unsymmetrical azo compounds is described by B. T. Gillis and J. D. Hagarty, J. Am. Chem. Soc., 87, 4576 (1965), where R is methyl. ##STR24##

NOVEL PROCESSES FOR AZO COMPOUNDS First Process

IA. ##STR25##

IB.

    R--NHNH.sub.2.HX + MCN + R.sub.1 C(O)R.sub.2  .sup.H.spsb.2O  B] + MX (1)

    [B]  .sup.O  (C).                                          (2)

where R is tert-alkyl or tert-aralkyl and R₁, R₂, and X are as defined above and M is an alkali metal.

When R is a primary and secondary alkyl radical, the [C] compounds are unstable and tautomerize to hydrazones [D]: ##STR26## This tautomerization of azo compounds, containing alpha hydrogens, to hydrazones is well known. The rate and extent of the tautomerization is highly dependent upon the nature of the R' and R" radicals and also the pH of the reaction medium. Most primary and secondary alkyl azo compounds tautomerize extremely fast in an acidic medium and the preferred method for oxidizing [B] compounds to the [C] products is with aqueous chlorine, a highly acidic medium. When R is a tertiary alkyl group, no alpha hydrogens are present and therefore no tautomerization occurs. Also, the [C] compounds where R is a primary and secondary alkyl and aralkyl group are not as useful as thermally sensitive free radical and gas generators because the [D] compounds, which would form upon heating [C], are thermally stable. Literature of interest in this area is:

Canadian Patent 655,296 issued January 1, 1963. J. S. Bevington and A. Wahid, Polymer 3, 585 (1962); ibid 4, 129 (1963).

D. Neighbors, et al, J. Am. Chem. Soc. 44, 1561 (1922). H. Zollinger, "Azo and Diazo Chemistry, Aliphatic and Aromatic Compounds," Interscience, New York, N.Y., 1961, p. 327.

In the first step of this "First IA" process, the defined hydrazine and define ketone are reacted in the presence of an inert solvent, preferably a benzene or like hydrocarbon, while the water produced is removed substantially continuously during the course of the reaction--in the case of benzene solvent the water goes overhead as a benzene-water azeotrope. The reaction is carried out at a temperature which will facilitate the preferred distillative removal of water.

In the second step of the First IA process, the hydrazone product [A] is reacted with hydrogen cyanide, preferably in the liquid state so as to act as a reaction medium also at a temperature of about 10° to about 80° C, preferably 45°-55° C, to form the cyanohydrazo product [B]. The reaction may also be carried out in the presence of an inert liquid, such as benzene and the like hydrocarbons, ethanol, and water. The reaction time will vary somewhat with the hydrazone and the temperature; 50°-60° C, for example 4-6 hours; at 25° C, as much as 18 hours.

In the final step of the First IA process, the hydrazo compound is oxidized under conventional conditions to the corresponding azo compound. For example, the hydrazo compound is contacted with aqueous solution of alkali metal hypohalite or aqueous chlorine at temperatures about the freezing point of water, e.g., 0°-10° C. Optionally, an organic solvent may also be present. Other oxidizing agent include: potassium permanganate, lead tetraacetate, ammonium nitrate, nitric acid, bromine, and the oxides of silver and mercury.

In "step 1" of the first IB process, the water soluble or partially water soluble ketone, the defined hydrazine acid salt and the cyanide are reacted in water at about 10°-80° C to form the cyanohydrazo product [B].

Other non-limiting details of this First process are to be found in certain working examples herein.

Second Process

II. ##STR27## where [A], R, R₁, and R₂ are as defined above and X₂ is bromine or chlorine.

In this Second Process tert-alkyl- or tert-aralkylhydrazones of ketones [A] and chlorine or bromine are reacted in the presence of an inert solvent, (i.e. a hydrocarbon, a chlorinated hydrocarbon or an aromatic hydrocarbon preferably a petroleum hydrocarbon) at temperatures from -60° C to +40° C, preferably -10° C to +30° C, to form the novel [P] compounds.

Other non-limiting details of this Second Process are to be found in certain working examples herein.

Third Process

III. ##STR28## where [P], R, R₁, R₂, M, Y, and Y" are as defined above. In this Third Process t-alkyl- and aralkylazo-α-halo-alkanes and aralkanes [P] are reacted with the active hydrogen compounds (Y--H or H--Y"--H) in the presence of a base or with the alkali or alkaline earth metal salt of the active hydrogen compound (MY or MY") in solvents, such as pentane, ether, tetrahydrofuran, glyme, alcohols, water, aqueous alcohols and acetone (the solvents, depending on the nature of MY or MY"), at temperatures of -10° C to 60° C, preferably 0° C to 30° C, to form the novel T-alkyl- and aralkylazo-α-substituted-alkanes and aralkanes [Q] and [Q¹ ].

Prior art relating to the Second and Third Processes is found in the following references:

Goldschmidt and Acksteiner, Ann. 618, 173 (1958)

British Patent 988,253 issued April 7, 1961 to Monsanto Co.

Canadian Patent 750,380 issued January 10, 1967 to Monsanto Co.

All of these references teach the following reactions: ##STR29## where: R^(IV) and R^(V) are selected from the class consisting of aliphatic, araliphatic, aromatic, cycloaliphatic and heterocyclic radicals having not more than about 22 carbons and R^(IV) and R^(V) taken together form cycloalkyl radicals; and

Y' is selected from the class consisting of: ##STR30##

Reaction (a) above is similar to the present Second Process except that the present process uses t-alkyl- and aralkylhydrazones (A) whereas reaction (a) above uses cyanoalkyl-hydrazones (D). The novelty of the present process (Second Process) is that it was unknown, prior to the present work, whether a non-cyano t-alkyl- and aralkylhydrazone would react with a halogen to form the novel t-alkyl- and aralkyl-a-haloazo compounds of structure (P).

We have not been able to prepare phenyl-α-haloazo-compounds from phenylhydrazones i.e. ##STR31## nor have we been able to prepare 3,5,5-trimethyl-3-chloropyrazoline-1 by chlorinating 3,5,5,-trimethylpyrazoline-2(a cyclic t-alkylhydrazone with chlorine. i.e. ##STR32##

Reaction (b) above is similar to the present Third Process except that the present process uses the novel (P) structures whereas reaction (b) above uses the α-cyanoalkyl-α'-haloalkylazo structures (R). The novelty again is that prior to the present work, it was unknown whether the novel compounds of structure (P) containing no α-cyano group would react with the above defined MY and MY" compounds to form the novel t-alkyl- and aralkyl-α-substituted azo compounds [Q] and [Q¹ ].

We have not been able to react ethoxycarbonyl-α-chloro-azo compounds with the MY and MY" compounds under the normal conditions to form the ethoxycarbonyl-α-substituted azo compounds. ##STR33## These α-chloro azo compounds were unreactive or decomposed under the above reaction conditions.

Other non-limiting details of the Third Process are to be found in certain working examples.

Fourth Process

IV. ##STR34## where R, R₃, R₄, and R₁₃ are as defined above and R₉ is a lower alkyl radical. A similar reaction for the case where the azo compound was a diester of azodicarboxylic acid to give azodicarbonamide derivatives is shown in the literature:

H. Bock and J. Kroner, Chem. Ber. 99, 2039(1966).

K. e. cooper and E. H. Ingold, J. Chem. Soc. 1926, 1894. ##STR35## It was unknown, prior to the present work, that a mono azo ester, such as [E], would react with primary and secondary amines (including ammonia) to form the corresponding azoformamide.

The [E] compounds, where R is a tertiary alkyl group, are known. They can be made from t-butylhydrazine and alkyl chloroformates followed by oxidation: ##STR36## The [N] compounds can also be prepared directly, without first forming the tertiary alkyl hydrazine, by the process covered in copending patent application Ser. No. 684,652 cited above.

This Fourth Process is preferably carried out in polar solvent such as ethanol, ether and methylene chloride. The reaction temperature is not critical but temperatures on the order of 0°-25° C are preferred. The working examples herein show that the reaction goes with ammonia, methylamine, dimethyl amine, ethylene diamine, glycine and ##STR37## glycine methyl ester, establishing the scope of HNR₃ R₄ and HN(R₃)R₁₃ N(R₃)H.

Other non-limiting details of the Fourth Process are to be found in certain working examples.

Fifth Process

IV. ##STR38## where R, R₅, and R₁₃ are defined as above. This reaction is novel for compounds where R is (R")₃ C-- as defined. The reason for this is that when R is a primary and secondary lower alkyl group, [G] is not formed in the first step but instead, [J] is formed as is described by: J. Lakritz, "The Synthesis and Reactions of Sterically Hindered Hydrazines; And the Acid Catalyzed Rearrangement of Tertiary Cyclic Azides," University of Michigan, Ph.D. thesis, 1960, University Microfilms, Inc., Mio 60-6898. ##STR39## The [J] compounds cannot be oxidized to azo compounds. The formation of [G] rather than [J] when R is a tertiary alkyl group is due to the bulky nature of the tertiary group. This has been previously reported and [G] compounds are known but have never been oxidized to the azo compounds. The azo compounds [H] are very unstable and therefore difficult to isolate.

Symmetrical azo compounds are known, these have been prepared from hydrazine and ##STR40## to obtain ##STR41## after oxidation. These azo compounds, however, are significantly different from the [H] compounds of the present invention.

The first step of the Fifth process may be carried out in water and in organic solvents that do not contain active hydrogens or carbonyl functions and in the presence of a base such as sodium hydroxide, sodium carbonate, tert.-amines, etc.

The second oxidation step of the Fifth process is carried out as discussed in connection with the First process.

Other non-limiting details of the Fifth process are to be found in certain working examples.

Sixth Process

VI. ##STR42##

The same chemistry as discussed in the Fifth Process above applies to the cases where "(R")₃ " is replaced by a primary and secondary lower alkyl group.

It has been observed that [M] behaves like the acid chlorides and that the operating conditions of the Fifth Process are applicable to this Sixth Process.

Other methods of preparing the α-hydroxyazoalkanes are described in copending application Ser. Nos. 453,451 (now abandoned in favor of Ser. No. 526,641 filed 11/26/74, which was abandoned in view of Ser. No. 664,604 filed 3/8/76) and 453,450, filed 3/21/74 of Ronald E. MacLeay and, entitled, respectively "Reduction Process For Making Azo Compound" and "Oxidation Process For Making Azo Compound."

2. Novel Hydrazo Compounds

The scope of the Hydrazo compounds of the invention has been set in the summary in connection with Formula II.

The discussion with respect to the tertiary group and the radicals R", R₃ and R₄ in connection with Formula I in the section on azo compounds is entirely applicable to Formula II. Compounds coming within the scope of Formula II are set out in the working examples.

Utility

The 1-(R"₃)C-semicarbazides (II) are useful compounds in the synthesis of compounds of Formula I where R' is ##STR43## since they can easily be oxidized to I by oxidizing agents such as potassium permanganate, chlorine or bromine.

Specific illustrations of this utility are given in the working examples.

Preparation Seventh Process

This process consists essentially of heating an aqueous solution of (R")₃ C-hydrazine or its acid salt with a urea, at a temperature of 50° - 110° C, preferably reflux temperature. For example:

VII. ##STR44## This reaction is broadly stated in the summary at Seventh Process.

Eighth Process

The reaction of a (R")₃ C-hydrazine with a cyanate or cyanic acid in an aqueous system constitutes the Eighth Process. For example:

VIII. ##STR45## This reaction is broadly stated in the summary at Eighth Process.

Other non-limiting details of these two hydrazo processes are set out in the working examples. 1-Aryl-semicarbazides have been prepared via the Seventh Process but the reaction cannot be generalized for all monosubstituted hydrazines. In the case of the arylhydrazines the unsubstituted nitrogen is the more basic nitrogen due to the electron withdrawing inductive effect of the phenyl group, e.g. ##STR46##

Literature of interest is:

A. andraca, Anales quim farm 1941, p. 15.

Pellizzari, Gazz. chim. ital. 16, 302 (1888) Pinner, Ber., 20, 2359

Beilstein, 15, 287

In the case of the monoalkylhydrazines the substituted nitrogen is the more basic nitrogen due to the electron donating effect of the alkyl substituent and reaction generally occurs with the substituted nitrogen in the absence of steric hindrance. In these cases reactions of the Eighth process produce 2-alkylsemicarbazides instead of 1-alkylsemicarbazides, e.g. ##STR47##

Literature of interest is:

C. vogelsange, Rec. trav. chim. 62, 5 (1943) K. A. Taipale and P. V. Usachev, J. Russ.

Chem. Soc. 62, 1241-58 (1930)

The 1-alkylsemicarbazides are generally prepared by reduction of the corresponding semicarbazones, a route not applicable for the synthesis of 1-(R")₃ C-semicarbazides as shown by Neighbors et al., supra. ##STR48##

No reference could be found in the literature for the preparation of 1-alkylsemicarbazides by the methods claimed. An attempt was made to prepare 1-methyl-semicarbazide by refluxing an aqueous solution of methylhydrazine hydrochloride and urea. No 1-methylsemicarbazide was produced.

EMBODIMENTS OF THE INVENTIONS

Numerous illustrative embodiments of the novel azo compounds, hydrazo compounds and novel processes described hereinbefore and utility thereof are presented in the following 83 working examples. It is to be understood that these examples although numerous are not to be considered as limiting the scope of the inventions as claimed.

EXAMPLE I

Preparation of alpha-(tert.-butylazo)isobutyronitrile

A. Alpha-(tert.-butylhydrazo)isobutyronitrile ##STR49##

To a stirred solution of 35.2 g. (0.28 m) tert.--butylhydrazine hydrochloride and 13.7 g. (0.28 m) sodium cyanide in 100 ml. of deionized water in a 200 ml. round bottom flask, was added 16.3 g. (0.28 m) acetone. The flask was stoppered and the reaction stirred overnight. The next morning the organic layer was separated, the aqueous layer extracted with 50 ml. methylene chloride and the methylene chloride layer and organic layer combined and dried over anhydrous sodium sulfate. The methylene chloride solution was filtered and the methylene chloride evaporated on a rotating evaporator. The yield was 42.1 g. (96.7%). The infra-red spectrum contained strong NH bands, a cyano band and did not contain any carbonyl or imino bands. Thus the infra-red spectrum was consistent with the structure of the desired product.

B. Alpha-(tert.-butylazo)isobutyronitrile ##STR50##

To 8.4 g. (.054 m) of alpha-(tert.-butylhydrazo) isobutyronitrile in a 4 neck 250 ml. round bottom flask was added with stirring dropwise 100 ml. of a solution containing 0.054 moles of sodium hypochlorite (prepared from 3.85 g. chlorine and 4.5 g. sodium hydroxide in water) holding the temperature below 5° C. with an ice bath. The reaction was stirred an additional twenty minutes after the addition was over and the organic layer separated. The organic layer was washed with 10 ml. of 5% HCl two 10 ml. portions of saturated NaHCO₃ solution, 10 ml. of deionized water, dried over anhydrous sodium sulfate and the product filtered. The yield was 6.0 g. (72.5%). The infrared spectrum did not contain any N-H bands and was consistent with the structure of the proposed product. The material assayed 99.6% by gas chromatographic analysis. It is a liquid and it is soluble in petroleum solvents.

Alpha-(tert.-butylazo)isobutyronitrile is a thermally sensitive free radical and gas generator. It produces 179 cc. of gas per gram at 110° C. The following half-life data have been determined:

    ______________________________________                                         temp.             t 1/2 (hrs.)                                                 ______________________________________                                          70° C.    40.5                                                         78.8° C.   10.0                                                          90° C.    2.0                                                          100° C.    0.54                                                         110° C.    0.20                                                         ______________________________________                                    

Example II

Polymerization of Styrene with alpha-(tert.-butylazo)isobutyronitrile

A solution of styrene containing 5 × 10⁻ ⁴ moles per deciliter of alpha-(tert.-butylazo)isobutyronitrile was heated at 85° C. and the change in density, which is a measure of polymer formation, was followed by means of a dilatometer to measure polymerization rates at 5% and 10% conversion to polystyrene. The rates obtained at 5% and 10% conversion were 9.73 × 10⁻ ³ and 9.22 × 10⁻ ³ moles per liter per minute respectively. Without the alpha-(tert.-butylazo)-isobutyronitrile, the 5 and 10% rates were 0.92 × 10⁻ ³ moles per liter per minute. Thus, this azo compound initiated the polymerization of styrene at 85° C.

EXAMPLE III

Curing an Unsaturated Polyester--Styrene Resin with alpha-(tert.-butylazo)isobutyronitrile

An unsaturated polyester resin was made by reacting maleic anhydride (1.0 mole), phthalic anhydride (1.0 mole), and propylene glycol (2.2 moles) until an acid number of 45-50 was obtained. To this was added hydroquinone at a 0.013% concentration. Seven parts of this unsaturated polyester was diluted with 3 parts of monomeric styrene to obtain a homogeneous blend having a viscosity of 13.08 poise and a specific gravity of 1.14.

To 20 grams of this blend was added 0.128 gram of alpha-(tert.-butylazo)isobutyronitrile and the resultant composition placed in a constant temperature bath at 212° F. (100° C.). The internal temperature was recorded as function of time and a peak exotherm of 424° F. (217.8° C.) was reached in 4.9 minutes indicating an excellent cure of the unsaturated polyesterstyrene resin blend had occurred. At 180° F. (82.2° C.), a peak exotherm of 381° F. (193.9° C.) was obtained in 13.3 minutes. The resultant cured materials were very hard.

Without an initiator, no cure of this resin blend occurred after more than 30 minutes at 212° F. (100° C.).

Example IV

Preparation of 1-tert.-butylazo-1-cycanocyclohexane

A. 1-tert.-butylhydrazo-1-cyanocyclohexane ##STR51##

To a rapidly stirred solution of 24.8 g. (0.2 m.) tert.-butylhydrazine hydrochloride and 9.8 g. (0.2 m.) sodium cyanide in 100 ml. of deionized water in a 250 ml. 4 neck round bottom flask, was added a solution of 19.6 g. (0.2 m.) of cyclohexanone in 15 ml. of ethanol. The reaction was stirred for 5 hours at room temperature and then allowed to stand overnight. The next morning the reaction was stirred an additional hour and filtered. The product was dried at 30° C. in a vacuum oven. The yield was 36.3 g. (93.5%) of a white solid melting at 70°-73° C. The white solid evolves HCN on exposure to air over extended periods. The infra-red spectrum contained strong NH bands, a cyano band and did not contain any carbonyl or imino bands. Thus the infra-red spectrum was consistent with the structure of the desired product.

B. 1-tert.-butylazo-1-cyanocyclohexane ##STR52##

To a rapidly stirred mixture of 39.0 g. (0.2 m.) 1-tert.-butylhydrazo-1-cyanocyclohexane, 200 ml. methylene chloride and 100 ml. water was added 14.3 g. (0.2 m.) chlorine at such a rate that the reaction temperature did not exceed 5° C. The reaction was stirred an additional 15 mins. after the addition was complete. The methylene chloride layer was separated, washed twice with 50 ml. portions of saturated NaHCO₃ solution, dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated on a rotating evaporator to obtain 35.0 g. of liquid product that assayed 86.5% by an ultra violet spectrophotometric analysis. Distillation gave a product, b.p. 71° C./1.2 mm. of Hg that assayed 97.6% as 1-tert.-butylazo-1-cyanocyclohexane. The infrared spectrum was in accord with this structure.

1-tert.-butylazo-1-cyanocyclohexane is a thermally sensitive free radical and gas generator. It produces 146 cc. of gas per gram at 130° C. The following half-life data have been determined:

    ______________________________________                                         temp.             t 1/2 (hours)                                                ______________________________________                                         96.3° C.   10.0                                                         100° C.    6.7                                                          110° C.    2.3                                                          120° C.    .75                                                          ______________________________________                                    

Example V

Polymerization of Styrene with 1-tert.-butylazo-1-cyanocyclohexane

The procedure of Example II was used at 85° C. and 100° C. The rates obtained at 5% and 10% conversion at 85° C. were 3.68 × 10⁻ ³ and 3.33 × 10⁻ ³ moles per liter per minute respectively and at 100° C. they were 13.3 × 10⁻ ³ moles per liter per minute. Without the 1-tert.-butylazo-1-cyanocyclohexane, the 5% and 10% rates at 100° C. were 2.81 × 10⁻ ³ moles per liter per minute.

Example VI

Curing an Unsaturated Polyester-styrene Resin with 1-tert.-butylazo-1-cyanocyclohexane

The procedure of Example III was used at 212° F. (100° C.) and 240° F. (115.6° C.) where peak exotherms of 414° F. (212.2° C.) and 440° F. (226.7° C.) were obtained after 10.0 and 5.3 minutes respectively using 0.2 gram of the 1-tert.-butylazo-1-cyanocyclohexane. The resultant cured resins were very hard.

Example VII

Preparation of 4-tert.-butylazo-4-cyano-2,6-dimethylheptane

A. tert.-butylhydrazone of diisobutylketone ##STR53## The tert.-butylhydrazone of diisobutylketone was prepared in 94.5% yield by heating a solution of 5.0 g. (.057 m) tert.-butylhydrazine, 8.1 g. (.057/m.) diisobutylketone and 0.1 g. p-toluene-sulfonic acid in benzene and azeotroping off the water formed in the reaction. The reaction was refluxed four hours and the benzene evaporated off on a rotating evaporator. The liquid product weighed 11.45 g. (94.5%) and the infrared spectrum was consistent with the proposed structure.

B. 4-tert.-butylhydrazo-4-cyano-2,6-dimethylheptane ##STR54##

4-tert.-butylhydrazo-4-cyano-2,6-dimethyl-heptane was prepared in 99% yield by heating a solution of 11.0 g. of diisobutylketone tert.-butylhydrazone in 20 ml. of liquid HCN at 50° C. for 6 hours. The excess HCN was evaporated off into a dry ice trap leaving 12.1 g. (99%) of the liquid product. The infra-red spectrum was consistent with the proposed structure of the compound (strong NH and weak CN bands).

C. 4-tert.-butylazo-4-cyano-2,6-dimethylheptane ##STR55##

To a rapidly stirred mixture of 12.1 g. (.046 m.) of 4-tert.-butylhydrazo-4-cyano-2,6-dimethylheptane, 30 ml. methylene chloride and 15 ml. water was added 7.35 g. (.046 m.) bromine at such a rate that the reaction temperature did not exceed 5° C. The reaction was stirred an additional 15 minutes after the addition was complete. The methylene chloride layer was separated, washed twice with 50 ml. portions of saturated NaHCO₃ solution, dried over anhydrous sodium sulfate, filtered, and the methylene chloride evaporated on a rotating evaporator to obtain 11.5 grams of liquid product. The infra-red spectrum was in accord with the structure of 4-tert.-butylazo-4-cyano-2,6-dimethylheptane.

4-tert.-butylazo-4-cyano-2,6-dimethylheptane is a thermally sensitive free radical and gas generator that begins to evolve nitrogen slowly at 70° C. At a 1.0 weight per cent loading it cured the unsaturated polyester-styrene resin of Example III at 180° F. (82.2° C.) giving a peak exotherm of 371° F. in 2.8 minutes and a very hard cured resin.

Example VIII

Preparation of 1-tert.-butylazo-1-cyano-3,3,5-trimethyl-cyclohexane

A. tert.-butylhydrazone of dihydroisophorone ##STR56##

The same procedure as was used in Example VII A was used for the preparation of dihydroisophorone tert.-butylhydrazone. The yield of liquid product was 12.0 g. (100%) and the infra-red spectrum was consistent with the structure of the proposed compound.

B. 1-tert.-butylhydrazo-1-cyano-3,3,5-trimethylcyclohexane ##STR57##

1-tert.-butylhydrazo-3,3,5-trimethylcyclohexane was prepared in the same manner as 4-tert.-butylhydrazo-4-cyano-2,6-dimethylheptane in Example VII B. The liquid product was used in the next step directly.

C. 1-tert.-butylazo-1-cyano-3,3,5-trimethylcyclohexane ##STR58##

1-tert.-butylazo-1-cyano-3,3,5-trimethylcyclohexane was prepared by bromine oxidation of the above 1-tert.-butylhydrazo-1-cyano-3,3,5-trimethylcyclohexane in the same way that 4-tert.-butylhydrazo-4-cyano-2,6-dimethylheptane was oxidized in Example VII C. The yield of liquid product was 8.2 g. (63%) and the infra-red spectrum was consistent with the structure of the proposed compound.

1-tert.-butylazo-1-cyano-3,3,5-trimethylcyclohexane is a thermally sensitive free radical and gas generator which begins to evolve nitrogen slowly at 100° C. At a 1.0 weight per cent loading it cured the unsaturated polyester-styrene resin of Example III at 180° F. (82.2° C.) giving a peak exotherm of 384° F. (195.6° C.) in 9.4 minutes and a very hard cured resin.

Example IX

Preparation of 2-tert.-butylazo-2-cyano-3,3-dimethylbutane ##STR59##

A. Pinacolone tert.-butylhydrazone

To a solution of 5 g. (0.05 m.) pinacolone in 50 ml. benzene was added 5 g. (0.057 m) tert.-butylhydrazine and a spatula tip of para-toluenesulfonic acid. The flask was fitted with a Dean Stark trap and the reaction refluxed until 0.9 ml. (0.05 m.) of water was azeotroped off. The solution was cooled down and the benzene stripped off leaving 8.5 g. (100%) of a white fluffy solid. The infra-red spectrum of the solid was consistent with the structure of the proposed compound.

B. 2-tert.-butylhydrazo-2-cyano-3,3-dimethylbutane

To a solution of 7.0 g. (0.0143 m.) of pinacolone tert.-butylhydrazone in 20 ml. of benzene in a pressure bottle was added 20 ml. of liquid HCN. The bottle was stoppered and the reaction heated at 50° C. for 4 hours. The reaction cooled down and the benzene and HCN stripped off. The yield was 8.0 g. of a crude solid. The solid was dissolved in pentane, the pentane solution dried over anhydrous sodium sulfate, filtered, and the pentane stripped off. The yield was 7.7 g. (94%) of a tan solid, melting range 67°-74° C. The infra-red spectrum was consistent with the structure of the proposed product.

C. 2-tert.-butylazo-2-cyano-3,3-dimethylbutane

To a mixture of 7.7 g. (0.039 m.) 2-tert.-butylhydrazo-2-cyano-3,3-dimethylbutane, 50 ml. methylene chloride and 25 ml. water, cooled to 0° in an ice bath, was added 6.25 g. (0.039 m.) bromine dropwise over 15 minutes holding the temperature at 0° to 5° C. After the bromine addition, the reaction was stirred 10 minutes, the methylene chloride layer separated, washed twice with 10% NaHCO₃ solution, dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated off. The yield was 7.6 g. (100%) of a white solid with a melting range of 38°-40° C. Its infra-red curve was in accord with the structure of 2-tert.-butylzao-2-cyan0-3,3-dimethylbutane. The product is a thermally sensitive free radical and gas generating compound that begins to evolve nitrogen at 95° C.

It cured the unsaturated polyester-styrene resin of Example III at 180° F. (82.2° C.) and 212° F. (100° C.) giving peak exotherms of 388° F. (197.8° C.) and 430° F. (221.1° C.) in 10.4 and 4.9 minutes respectively. The cured samples were very hard.

Example X

Preparation of alpha-tert.-butylazo-alpha-methyl-gammacarboxybutyronitrile ##STR60##

To a mixture of 5.1 g. (0.0438 m.) levulinic acid in 25 ml. water was added in the following sequence: 3.52 g. (0.0438 m.) 50% sodium hydroxide, 2.94 g. (0.06 m.) sodium cyanide and 5.45 g. (0.0438 m.) tert.-butylhydrazine hydrochloride. The reaction mixture was stirred for 5 hours at room temperature, cooled to 5° C. and chlorine passed into the system holding the temperature below 15° C. until there was an increase in weight of 5.0 g. (0.07 m.). After the chlorination was over, the product was extracted with methylene chloride, the methylene chloride solution washed twice with water, dried over anhydrous sodium sulfate, filtered, and the methylene chloride evaporated off on a rotating evaporator. The crude yield was 4.85 g. (52.5%). The crude material was recrystallized from benzene-pentane to give 4.0 g. of product having a melting range of 79°-81° C. The infra-red spectrum was consistent with the structure of the proposed compound.

Alpha-tert.-butylazo-alpha-methyl-gammacarboxybutyronitrile is a thermally sensitive free radical and gas generating compound which begins to evolve nitrogen at 85° C. The half-life of this compound is 551/2 hours at 65° C., 11.0 hours at 75° C. and 3.15 hours at 85° C.

It cured the unsaturated polyester-styrene resin of Example III at 180° F. (82.2° C.) and 212° F. (100° C.) at a 1.0 weight per cent loading giving peak exotherms of 410° F. (210.0° C.) and 422° F. (216.7° C) in 8.5 and 3.8 minutes respectively. The cured samples were very hard.

Example XI

Preparation of alpha-(tert.-cumylazo)isobutyronitrile

A. Alpha-(tert.-cumylhydrazo)isobutyronitrile ##STR61##

The tert.-cumylhydrazone of acetone (19.0 g.) was treated with an aqueous solution of excess hydrocyanic acid at R.T. This mixture was stirred for 6 hours and then allowed to stand overnight. The reaction mixture was then extracted with methylene chloride. The methylene chloride extracts were dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated to obtain a product (21.5 g.) that had an infra-red spectrum in accord with the structure of alpha-(tert.-cumylhydrazo)isobutyronitrile. The product was used without further purification in the next step.

B. Alpha-(tert.-cumylazo)isobutyronitrile ##STR62##

The crude hydrazo product from above (21.4 g.) was dissolved in 100 ml. methylene chloride, 50 ml. of water added and the mixture cooled to 0°0 C. Chlorine was passed into the solution at 0.4 g./min. until 7.1 g. of chlorine has been added. The temperature was held at 0°-3° C. throughout the addition. At the end of the addition the methylene chloride layer was separated, washed twice with saturated, NaHCO₃, dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated leaving 18.6 g. of crude alpha-(tert-cumylazo)isobutyronitrile. A sample of the crude alpha- (tert-cumylazo)isobutyronitrile (8.75 g.) was chromatographed through aluminia and 6.0 g. of the pure liquid alpha-(tert-cumylazo)isobutyronitrile was obtained as evidenced by infra-red spectroscopy.

Alpha-(tert-cumylazo)isobutyronitrile is a thermally sensitive free radical and gas generator which begins to evolve nitrogen slowly at 55° C.

At a 1.0 weight per cent loading, it cured the unsaturated polyester-styrene resin of Example III at 180° F. (82.2° C.) giving a peak exotherm of 378° F. (192.2° C.) in 1.3 minutes and a very hard cured resin.

Example XII

Preparation of alpha-tert-butylazo-alpha-cyclopropylpropionitrile

A. Tert-butylhydrazone of methyl cyclopropyl ketone ##STR63##

The same procedure as was used in Example VII A was used for the preparation of methyl cyclopropyl ketone tert-butylhydrazone. The yield of liquid product was 8.8 g. (100%) and the infra-red spectrum was consistent with the structure of the proposed compound.

B. Alpha-tert-butylhydrazo-alpha-cyclopropylpropionitrile ##STR64##

A solution of 8.7 g. methyl cyclopropyl ketone tert-butyl-hydrazone in 20 ml. liquid hydrocyanic acid was heated for 6 hours in a pressure bottle at 60 ° C. The solution was cooled, poured into ice water and the aqueous solution extracted twice with ether. The ether extracts were combined, washed with saturated sodium bicarbonate solution dried over sodium sulfate, filtered and the ether evaporated off. The yield was 10.0 g. (99%) of a brown liquid. The infra-red spectrum was consistent with the structure of the proposed product.

C. Alpha-tert-butylazo-alpha-cyclopropylpropionitrile ##STR65##

To a mixture of 10.0 g. (0.055 m.) of crude alpha-tert-butylhydrazo-alpha-cyclopropionitrile, 100 ml. methylene chloride, and 50 ml. water, cooled to 0° C. in an ice bath, was added 8.75 g. (.055 m.) of bromine dropwise over 15 minutes holding the temperature at 0° to 5° C. After the bromine addition, the reaction was stirred 10 minutes, the methylene chloride layer separated, washed twice with saturated sodium bicarbonate solution, dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated off. The yield was 8.9 g. (90%) of a brown liquid. The liquid was chromatographed over an alumina column, eluting it with pentane, to give 8.1 g. of a light tan liquid which solidifies in the freezer. The infra-red spectrum was consistent with the structure of the proposed compound. The product is a thermally sensitive free radical and gas generating compound that begins to evolve nitrogen at 75° C.

Alpha-tert.-butylazo-alpha-cyclopropyl propionitrile cured the unsaturated polyester-styrene resin of Example III at 180° F. (82.2° C.) and 212° F. (100° C.) giving peak exotherms of 403° F. (206.1° C.) and 420° F. (215.6° C.) in 3.3 and 2.1 minutes respectively. The cured samples were very hard.

EXAMPLE XIII

Preparation of tert.-butylazoformamide ##STR66##

Ammonia gas was slowly bubbled into a solution of 5.4 g. (0.0314 m.) of isopropyl tert.-butylazocarboxylate in 25 ml. of 95% ethanol holding the temperature at 10° C. ± 5° with an ice bath. The ammonia addition was continued 5 minutes after the exotherm subsided. The reaction was stirred an additional hour at room temperature and the alcohol evaporated off on the rotating evaporator. The crude residue was slurried in 10 ml. pentane and the crystals filtered off. The yield was 3.4 g. (84%) of a yellow solid (m.p. 103°-105° C.) that assayed 98.3% by an iodometric titration. The infra-red spectrum is consistent with the structure of tert.-butylazoformamide.

Tert.-butylazoformamide is a thermally sensitive free radical and gas generator. The following half-life data have been determined by gas evolution technique using trichlorobenzene as the solvent:

    ______________________________________                                         temp.° C.  t 1/2 (hours)                                                ______________________________________                                         150°       0.14                                                         130°       0.87                                                         120°       3.00                                                         110°       5.73                                                         ______________________________________                                    

It cured the unsaturated-polyester-styrene resin of Example III at a 1.0 weight per cent loading at temperature of 212° F. (100° C.), 240° F. (115.6° C.), and 265° F. (129.4° C.) giving peak exotherms of 407° F. (208.0° C.), 430° F. (221.1° C.), and 438° F. (225.6° C.) in 7.1, 5.9, and 4.5 minutes respectively. The cured samples were very hard.

EXAMPLE XIV

Preparation of tert.-butylazo-N-methylformamide ##STR67##

Methylamine was slowly bubbled into a solution of 5.0 g. (0.0346 m.) methyl tert.-butylazocarboxylate in 25 ml. of 95% ethanol holding the temperature at 10° C. ± 5° C. with an ice bath. The methylamine addition was continued 5 minutes after the exotherm subsided. The reaction was stirred an additional one-half hour at room temperature and the ethanol and excess methylamine were evaporated off on the rotating evaporator. The yield was 5.0 g. (100%) of crude material or 4.6 g. (92%) after washing with pentane. The purified product has a melting range of 34° - 36° C. and assayed 97.7% by an iodometric analysis. The infra-red spectrum was consistent with the structure of tert.-butylazo-N-methylformamide.

It cured the unsaturated polyester-styrene resin of Example III at a 1.0 weight per cent loading at 265° F. (129.4° C.) giving a peak exotherm of 428° F. (220.0° C.) in 17.1 minutes and a very hard cured resin.

EXAMPLE XV

Preparation of tert.-butylazo-N,N-dimethylformamide ##STR68##

Dimethylamine was slowly bubbled into a solution of 5.0 g. (0.0346 m.) methyl tert.-butylazo-carboxylate in 25 ml. of 95% ethanol holding the temperature at 10° C. ± 5° with an ice bath. The dimethylamine addition was continued 5 minutes after the exotherm subsided. The reaction was stirred an additional one half hour at room temperature and the ethanol and excess dimethylamine were evaporated off on the rotating evaporator. The yield was 5.45 g. (100%) of a yellow liquid which crystallized in the freezer. The material assayed 92.1% by an iodometric analysis and the infra-red spectrum was consistent with the structure of tert.-butylazo-N,N-dimethylformamide.

The product is useful oxidizing agent as evidenced by the fact that it oxidized iodide ion to free iodine.

EXAMPLE XVI

Preparation of tert.-butylazo-N-carbmethoxymethylformamide ##STR69##

To a solution of 3.4 g. (0.27 m.) of the hydrochloride of glycine methyl ester in 20 ml. water was added 2.16 g. (0.027 m.) 50% sodium hydroxide. The solution was cooled to 5° C. and a slow addition of 3.75 g. (0.026 m.) methyl tert.-butylazocarboxylate in 15 ml. ethanol begun. The addition required 15 minutes and the reaction was stirred an additional 2 hours after the addition was over. The homogeneous solution was then poured into 50 ml. water and the aqueous solution extracted three times with methylene chloride. The methylene chloride layers were combined, dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated off. The yield was 4.35 g. (83%) of a yellow solid. The crude product was recrystallized from benzene-pentane. The recrystallized material had a melting range of 88°-90° C. and assayed 99.0% by an iodometric titration.

The infra-red spectrum is consistent with the structure of tert.-butylazo-N-carbmethoxymethylformamide. The product is a thermally sensitive free radical and gas generating compound that begins to evolve nitrogen at 140° C. It is also an oxidizing agent that oxidized iodide ion to free iodine.

It cured the unsaturated polyester-styrene resin of Example III at a 1.0 weight per cent loading at 240° F. (115.6° C.) and 265° F. (129.4° C.) giving peak exotherms of 356° F. (180.0° C.) and 484° F. (251.1° C.) in 15.8 and 5.1 minutes respectively. The cured samples were very hard.

EXAMPLE XVII

Preparation of tert.-butylazo-N-carboxymethylformamide ##STR70##

To a solution of 3.0 g. (0.04 m.) glycine in 30 ml. water was added 3.2 g. (0.04 m.) 50% sodium hydroxide. The solution was cooled to 5° C. and a slow addition of 5.0 g. (0.0337 m.) methyl tert.-butylazocarboxylate in 10 ml. ethanol begun. The addition required 15 minutes and the reaction was stirred an additional 2 hours at room temperature. A few drops of 50% sodium hydroxide were added and the solution extracted with methylene chloride to remove any unreacted methyl-tert.-butylazocarboxylate. The methylene chloride layer was colorless and was discarded. The aqueous layer was made acidic (pH = 2) by adding concentrated hydrochloric acid and extracted with 4 - 50 ml. portions of methylene chloride. The methylene chloride layers were combined, dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated off. The yield was 5.5 g. (86.5%) of a yellow viscous liquid which crystallized on standing in the freezer. The crude product assayed 77.4% by an iodometric analysis and the infra-red spectrum was consistent with the structure of tert.-butylazo-N-carboxymethylformamide. The product is a thermally sensitive compound that begins to evolve nitrogen at 60° C. It is also an oxidizing agent that oxidized iodide ion to free iodine.

EXAMPLE XVIII

Preparation of tert.-cumylazoformamide

A. 1-tert.-cumyl-2-carbisopropoxyhydrazine ##STR71##

A solution of 12.3 g. (0.051 m.) of the oxalic acid salt of tert.-cumylhydrazine was slurried in 100 ml. water and the solution made basic by adding 17.0 g. (0.212 m.) of 50% sodium hydroxide. The resulting sodium oxalate was filtered off, washed with 25 ml. water and the filtrate transferred to a reactor.

To the rapidly stirred solution was added 6.25 g. (0.0512 m.) isopropyl chloroformate and the reaction stirred at room temperature for an additional 3 hours. Methylene chloride (100 ml.) was added and the reaction stirred an additional hour, the methylene chloride layer separated and the aqueous phase extracted twice with 100 ml. methylene chloride. The methylene chloride layers were combined, dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated off on a rotating evaporator. The yield was 10.8 g. (89.5%) of a viscous liquid. The infra-red spectrum was consistent with the structure of the proposed compound.

B. Isopropyl tert.-cumylazocarboxylate ##STR72##

To a solution of 10.8 g. (0.0458 ) of crude 1-tert.-cumyl-2-carbisopropoxyhydrazine in 100 ml. methylene chloride was added 50 ml. water and the mixture cooled to 5° C. Bromine, 8.0 g. (0.050 m.), was added dropwise to this stirred mixture holding the temperature at 5° - 10° C. with an ice bath. The reaction was stirred an additional 15 minutes at 5° C. The methylene chloride layer separated, washed twice with NaHCO₃ solution, dried over anhydrous sodium sulfate and the methylene chloride evaporated off on a rotating evaporator. The product was placed in the freezer for an hour and a small amount of white solid crystallized out. The product was filtered, the solid washed with pentane, and the pentane evaporated from the filtrate. The yield was 9.8 g. (91.5%) of a yellow liquid. The infra-red spectrum of the product was in agreement with the structure of the proposed compound. The product assayed 88.5% by an iodometric titration.

Isopropyl tert.-cumylazocarboxylate is a thermally sensitive compound and slowly evolves nitrogen at 80° C.

C. Tert.-cumylazoformamide ##STR73##

To a solution of 4.9 g. (0.0185 m.) of 88.5% isopropyl tert.-cumylazocarboxylate in 25 ml. ethanol, cooled to 5° C. in an ice bath, was passed a slow stream of ammonia. There was a slight exotherm and the temperature slowly rose to 15° C. When the temperature began to drop the ammonia addition was stopped. The reaction was stirred an additional 15 minutes and the yellow solid which formed was filtered off. The filtrate was evaporated to dryness and the resulting yellow solid washed with pentane to remove any unreacted isopropyl cumylazocarboxylate. The two crops were combined and the yield was 3.2 g. (90.5%). The yellow solid was recrystallized from benzene. The melting range of the recrystallized material was 140° - 143° C. and it assayed 100% by an iodometric titration.

Tert.-cumylazoformamide is a thermally sensitive free radical and gas generating compound. It rapidly evolves nitrogen upon melting. It oxidized iodide ion to free iodine. It cured the unsaturated polyester-styrene resin of Example III at a 1.0 weight per cent loading at 240° F. (115.6° C.) and 265° F. (129.4° C.) giving peak exotherms of 422° F. (216.7° C.) and 454° F. (234.4° C.) in 10.3 and 6.0 minutes respectively. The cured samples were very hard.

EXAMPLE XIX

Preparation of Pivaloyl tert-butyldiimide

A. 1-Pivaloyl-2-tert.-butylhydrazine ##STR74##

A solution of 40.8 g. (0.33 m.) of tert.-butylhydrazine hydrochloride in 300 ml. of distilled water was placed in a 500 ml. 4 neck, round bottom flask equipped with a high speed mechanical stirrer, a thermometer and a condenser, and cooled to 10° C. The solution was made basic by adding 24.3 g. (0.225 m.) of sodium carbonate and then 18.9 g. (0.15 m.) of pivaloyl chloride was added dropwise over 1 hour holding the temperature below 10° C. with an ice bath. The mixture was stirred for 3 hours and the white solid which formed was filtered off and dried. The product weight 16.5 g. after drying and had a melting range of 97° - 105° C.

The aqueous filtrate was extracted with methylene chloride, the methylene chloride solution dried and the methylene chloride evaporated off on a rotating evaporator. The resultant solid weighed 5.9 g. and had a melting range of 98° -101° C. The infra-red spectra of the two solids were identical and were also consistent with the structure of 1-pivaloyl 2-tert.-butylhydrazine. The total yield was 22.4 g. (86.5%).

B. Pivaloyl tert.-butyldiimide (or pivaloyl azo isobutane) ##STR75##

To a solution of 5.9 g. (0.0343 m.) of 1-pivaloyl-2-tert.-butylhydrazine in 100 ml. of methylene chloride cooled to 5° C., was added 75 ml. of a sodium hypochlorite solution as fast as possible without exceeding a reaction temperature of 5° C. The sodium hypochlorite solution was prepared by adding 2.4 g. (0.0343 m.) chlorine to 75 ml. of a solution containing 2.7 g. of (0.0686 m.) of sodium hydroxide. The reaction was stirred an additional 10 minutes at 5° C. after the addition of the sodium hypochlorite solution. The methylene chloride layer was separated. The methylene chloride solution was washed once with sodium bicarbonate solution, dried over anhydrous sodium sulfate, filtered, and the methylene chloride evaporated off on the rotating evaporator. An orange liquid with a solid suspended in it was obtained. Pentane (20 ml.) was added to the solution and the solution cooled in the freezer. The pentane solution was filtered and the filtrate evaporated to dryness leaving 2.0 g. (36%) of the liquid pivaloyl tert.-butyldiimide. The product assayed 77.7% by an iodometric titration and its infra-red spectrum was consistent with the proposed structure.

The white solid was not identified; it is thought to be a decomposition product.

Pivaloyl tert.-butyldiimide is a thermally unstable compound and evolves nitrogen at 35° C. It cured the unsaturated polyester-styrene resin of Example III at a 1.0 weight per cent loading at room temperature and at 180° F. (82.2° C.) giving peak exotherms of 139° F. (59.4° C.) and 289° F. (142.8° C.) in 34.1 and 4.9 minutes respectively. The 180° F. (82.2° C.) cured sample was very hard.

EXAMPLE XX

Preparation of Benzoyl tert.-butyldiimide

A. 1-Benzoyl-2-tert.-butylhydrazine ##STR76##

1-benzoyl-2tert.-butylhydrazine was prepared in 71% yield by adding benzoyl chloride to a basic solution of t-butylhydrazine in water. The procedure was the same as that for preparing 1-pivaloyl-2-tert.-butylhydrazine in Example XIX A. The product has a melting range of 94° - 95° C. and its infra-red spectrum was consistent with that of the proposed structure.

B. Benzoyl tert.-butyldiimide ##STR77##

Benzoyl tert.-butyldiimide was prepared by the oxidation of 1-benzoyl-2-tert.-butylhydrazine with sodium hypochlorite in the same manner as the preparation of pivaloyl tert.-butyldiimide in Example XIII B. The yield was 40% of red liquid benzoyl tert.-butyldiimide which assayed 71.7% by an iodometric analysis and its infra-red spectrum was consistent with the proposed structure.

The solid impurities present in the crude azo were not identified but they are thought to be decomposition products since their infra-red spectrum was different from the starting hydrazo compound.

Benzoyl tert.-butyldiimide is a thermally unstable compound and evolves nitrogen at 25° C. It cured the unsaturated polyester-styrene resin of Example III at a 1.0 weight per cent loading at 180° F. (82.2° C.) giving a peak exotherm of 233° F. (112.0° C.) in 10.0 minutes and a hard cured resin.

EXAMPLE XXI

Preparation of 2,4,6-tri-(tert.-butylazo)-1,3,5-triazine

A. 2,4,6-Tri-(tert.-butylhydrazo)-1,3,5-triazine ##STR78##

To a solution of 5.55 g. (0.06 mole) of 95% tert.-butylhydrazine in 25 ml. of anhydrous ether at 5° to 10° C. was added, with stirring, a solution of 1.85 g. (0.01 mole) of cyanuric chloride in 35 ml. of anhydrous ether from a dropping funnel. The addition rate was such that the temperature was maintained at around 10° C. The stirred reaction mixture was then slowly warmed to room temperature where it was allowed to stand overnight. The mixture was then filtered. The solid filter cake was triturated with water and the resultant water washed white solid dried to obtain 0.62 g. (18.3% yield) of product, m.p. 189° -190° C., having an infra-red spectrum that was in accord with the structure of 2,4,6-tri-(tert.-butylhydrazo)-1,3,5-triazine.

B. 2,4,6-Tri-(tert.-butylazo)-1,3,5-triazine ##STR79##

0.55 g. of the above 2,4,6-tri-(tert.-butylhydrazo)-1,3,5-triazine was dissolved in 50 ml. of water to which 1 ml. of concentrated hydrochloric acid was added. The resultant solution was cooled to below 5° C. and then 0.115 g. of chlorine gas was admitted over a 21/2 minute period. The reaction mixture was stirred at 5° C. for another 15 minutes and then allowed to stand at 5° C. for one hour. Then 75 ml. of ether were added. The reaction mixture was stirred and then the ether layer separated. The water layer was washed with ether and the combined ether layers washed with saturated aqueous sodium chloride until the water extracts were neutral. The ether solution was dried over anhydrous sodium sulfate, filtered, and the ether evaporated under vacuo to obtain 0.47 g. (86% yield) of a viscous red liquid product that assayed 100% for 2,4,6-tri-(tert.-butylazo)-1,3,5-triazine by an iodometric titration. Its infrared spectrum was in accord with the proposed structure.

2,4,6-Tri-(tert.-butylazo)-1,3,5-triazine is a thermally sensitive free radical and gas generator that begins to evolve nitrogen slowly at 102° C. This product is also useful as an oxidizing agent as evidenced by the fact that it oxidized iodide ion to free iodine.

EXAMPLE XXII

Preparation of 2(-tert.-butylazo)propene ##STR80##

To a solution of 6.75 g. (0.077 m.) tert.-butylhydrazine in 50 ml. of methylene chloride containing 2 g. of anhydrous sodium sulfate, was added 3.0 g. (0.0326 m.) chloroacetone. The addition was carried out dropwise holding the reaction temperature below 10° C. with an ice bath. The reaction was stirred an additional 45 minutes and filtered. The filtrate was washed with cold water (10° C.), dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated off using a rotating evaporator and a 20° C. water bath. A yellow oil containing some solids suspended in it was obtained. The crude material was slurried in cold pentane and filtered. The pentane was then evaporated off from the filtrate on the rotating evaporator. The yield was 1.9 g. (47%) of a yellow oil. The infra-red spectrum was consistent with the structure of the proposed compound. 2-tert.-butylazopropene is a thermally unstable compound and evolves nitrogen at room temperature and is therefore a very low temperature blowing agent.

EXAMPLE XXIII

Preparation of 1(-tert.-butylazo)cyclohexene ##STR81##

To a solution of 11 g. (0.125 m.) tert.-butylhydrazine in 80 ml. of methylene chloride containing 2 g. anhydrous sodium sulfate, was added 6.8 g. (0.052 m.) alpha-chlorocyclohexanone. The addition was carried out dropwise and the reaction temperature was maintained at 20° ± 5° C. by an ice bath. The solution immediately turned yellow, but the reaction was stirred for an additional 1 hour after the addition was complete before filtering it. The filtered methylene chloride solution was washed with 100 ml. water, dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated off. A viscous, gelatinous liquid remained. The material was cooled in the freezer and then filtered. A white solid, 0.1 g., remained on the filter. The filtrate weighed 8.4 g. (97% yield) and its infra-red spectrum was consistent with the proposed structure. It showed the absence of N-H and carbonyl bands and the presence of a carbon-carbon double bond (1,650 cm⁻ ¹) and a conjugated azo bond (1,510 cm⁻ ¹).

The product evolves nitrogen at 60° C.

1(-tert.-butylazo)cyclohexene gelled the unsaturated polyester-styrene resin of Example III at room temperature.

EXAMPLE XXIV

Preparation of 1-tert. butylazo-1-carbamylcyclohexane ##STR82##

To 100 ml. of 95% H₂ SO₄ in a 4 neck 250 ml. round bottom flask, cooled to -5° C. in a salt-ice bath, was added 23.0g. (0.119 m.) of 1-tert. butylazo-1-cyanocyclohexane over a 1/2 hour period holding the temperature between -5° and 0° C. during the addition. The temperature was allowed to slowly rise to 20° C. over 1 hour, stirred 1 hour at 20° C. and finally stirred for 3 hours at 25° C. The acid solution was then added slowly to 750 ml. of rapidly stirred cold water, holding the temperature of the water between 10° and 15° C. The reaction was stirred one half hour and filtered. The filter cake was washed acid free with water and dried. After drying it was slurried in 50 ml. pentane and filtered. The yield was 17.3g. of a light yellow solid with a melting range of 86° -92° C. (91°-93° C. after recryst. from benzene-pentane). The percent yield was 69%. The pentane filtrate was stripped to dryness leaving 4.4g. of unreacted starting material. The corrected percent yield was 85.5%. The infrared spectrum of the product was consistent with the structure of 1-t-butylazo-1carbamylcyclohexane.

1-t-butylazo-1-carbamylcyclohexane is a thermally sensitive free radical and gas generator. It evolves nitrogen above 120° C. It cured the unsaturated-polyester-styrene resin of Example III at a 1.0 weight per cent loading at 240° F. (115.6° C.) giving a peak exotherm of 444° F. (228.9° C.) in 6.8 minutes.

EXAMPLE XXV

Preparation of 2-t-butylazo-2-carbamylpropane ##STR83##

The method of preparing 2-t-butylazo-2-carbamylpropane from alpha(t-butylazo)-isobutyronitrile was the same as that used in example XXIV for the preparation of 1-t-butylazo-1-carbamylcyclohexane. The product was a white solid having a melting range of 80°-82° C. The infrared spectrum of the product was consistent with the structure of 2-t-butylazo-2-carbamylpropane.

2-t-butylazo-2-carbamylpropane is a thermally sensitive free radical and gas generator. It evolves nitrogen above 120° C. It cured the unsaturated-polyesterstyrene resin of Example III at a 1.0 weight per cent loading at 240° F. (115.6° C.) giving a peak exotherm of 442° F. (227.8° C.) in 5.7 mins.

EXAMPLE XXVI

1-t-butylsemicarbazide ##STR84##

A. Urea Process

To a solution of 48g. (0.386m) tert-butylhydrazine hydrochloride in 200 ml. water was added 72g. (1.2m) urea and the solution refluxed for 4 hours, cooled to 5° C. and filtered. The filter cake was recrystallized from 100 ml. water and dried. The yield was 42.3g. (83.5%) of a white crystalline solid with a melting range of 200°-202° C. The infrared spectrum was in agreement with the structure of 1-t-butylsemicarbazide.

B. Cyanate Process

To a solution of 8.8g. (0.1m) t-butylhydrazine in 50 ml. water was added 50 ml. of an aqueous solution containing 8.1 g. (0.1m) potassium cyanate. The mixture was stirred overnight, about 12 hours, at room temperature, about 25° C., cooled to 5° C. and filtered. The filter cake after drying weighed 11.6g. (89%) and had a melting range of 203°-204° C. The infrared spectrum was in agreement with the structure of 1-t-butylsemicarbazide.

EXAMPLE XXVII

t-butylazoformamide ##STR85##

To a slurry of 5.0g. (0.038m) 1-t-butylsemicarbazide, 75 ml. methylene chloride, and 50 ml. saturated salt solution held at 5° C. by an ice bath was added 4.0g. (0.025m) potassium permanganate in small increments over 20 minutes. After the addition was complete, the reaction was stirred an additional one half hour at 5°-10° C. and the methylene chloride layer separated. The aqueous layer was extracted with an additional 75 ml. methylene chloride, the methylene chloride layers combined, dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated off on a rotating evaporator. The yield was 4.9g. (99%) of a yellow crystalline solid with a melting range of 103°-105° C. which assayed 100% by an iodometric titration. The infra-red spectrum is consistent with the structure of t-butylazoformamide.

Example XXVIII

Polymerization of Ethyl Acrylate with α-tert-Butylazo-α-methyl-γ-carboxybutyronitrile and its Sodium Salt.

An emulsion containing 50 g. of deionized water, 40 g. ethyl acrylate, 4.8 g. Triton X-200, Rohm & Haas anionic surfactant, and 0.0769 g. (3.65 × 10⁻ ⁴ moles) α-tert-butylazo-α-methyl-γ-carboxy-butyronitrile (from Example X) was prepared. Approximately 25 g. of the emulsion was placed in a 250 ml. 4-neck round bottom flask equipped with a mechanical stirrer, thermometer and condenser. Nitrogen was passed through the system and the contents of the flask were heated to the reflux temperature of 82° C. When the temperature rose to 90° C., indicating polymerization was occurring, the balance of the emulsion was slowly added from a self-venting addition funnel, maintaining the temperature at 85°-87° C. At the end of the addition the temperature was raised to 95° C. for 5 minutes, a very small amount of hydroquinone added and the reaction cooled to room temperature. The total reaction times was 11/3 hours. The final pH was 3.6. A 5 g. aliquot was weighed into a tared dish and the monomers and water evaporated and the conversion of monomer to polymer was determined to be 94%.

A similar polymerization was run under the same conditions using 3.65 × 10⁻ ⁴ moles of the sodium salt of α-tert-butylazo-α-methyl-γ-carboxybutyronitrile as the initiator. The conversion was 92.3% and the final pH was 6.6.

A similar polymerization ran under the same conditions for 3 hours with no initiator gave only 31/2% conversion.

General procedures (GP) for the preparation of the compounds listed as Examples XXIX to L in Table 1 are set out below.

(GP 1) Preparation of t-Butylazo-α-chloro-alkanes and aralkanes of Examples XXIX to XXXIV.

Into a solution of .05 moles of the t-butylhydrazone of the appropriate ketone in 40 ml. of pentane in a 100 ml. flask, precooled at about -10° C. in an ice bath, was passed 0.025 moles of chlorine over 20 minutes. When the addition was complete, the reaction was stirred an additional 1/2 hour and the insoluble t-butylhydrazone hydrochloride filtered off. The pentane solution was washed with ice water to remove any residual hydrochloride, dried and the pentane removed on a rotating evaporator. Structure proofs were determined by infrared spectroscopy.

The t-butylhydrazone hydrochloride can be converted back to the t-butylhydrazone with sodium bicarbonate in water.

(GP 2) Preparation of t-Butylazo- α-methoxy-alkane and aralkanes of Examples XXXV to XL.

To a solution of .02 moles of 50% NaOH in 20 ml. of methanol, cooled to 5° C. in an ice bath, was added .015 moles of the desired t-butylazo-α-chloro compound over 5-10 minutes. The reaction was stirred an additional one-half hour and poured into 50 ml. cold water. The product was extracted out of the water with 50 ml. pentane. The pentane solution was dried over anhydrous Na₂ SO₄, filtered and the pentane evaporated. Structure proofs were determined by infrared spectroscopy.

(GP 3) Preparation of t-Butylazo-α-azido-alkanes and aralkanes of Examples XLI to XLV.

To a solution of .08 moles of sodium azide in 15 ml. water was added 76 ml. of acetone. The resulting mixture was cooled to 5° C. and .015 moles of the desired t-butylazo-α-chloro compound was added dropwise over 5- 10 minutes. The reaction was stirred an additional one-half hour at 5° C and poured into 150 ml water. The organic layer was extracted with pentance, dried over anhydrous Na₂ SO₄, filtered and the pentane evaporated. Structure proofs were determined by infrared spectroscopy.

(GP 4) Preparation of t-Butylazo-α-t-butylperoxyalkanes and aralkanes of Examples XLVI to L.

Into a solution of 2.0 g. (.05 m) of sodium hydroxide in 20 ml methanol at 5° C was added 5.4 g (.055 m) of 90.3% t-butylhydroperoxide and the solution stirred for 15 minutes. To this solution was added 0.04 moles of the desired t-butylazo-α-chloro-alkane over 5-10 minutes, holding the temperature at 5° C with an ice bath. The reaction was stirred an additional one-half hour at 5° C and poured into 100 ml water. The product was extracted with 50 ml pentane and the pentane solution washed with 50 ml of 10% KOH solution, water until neutral, dried over anhydrous sodium sulfate, filtered and the pentane evaporated off. Structure proofs were determined by infrared spectroscopy.

                                      Table I                                      __________________________________________________________________________                                   STRUCTURE                                                                       ##STR86##                                       EXAMPLE     NAME              Z    R.sub.1                                                                            R.sub.1  YIELD                          __________________________________________________________________________     XXIX  1-t-butylazo-1-chlorocyclohexane                                                                       Cl   (CH.sub.2).sub.5                                                                            52.5%                          XXX   2-t-butylazo-2-chloro-4-methylpentane                                                                  CL   CH.sub.3                                                                           i-C.sub.4 H.sub.9                                                                       98.7%                          XXXI  4-t-butylazo-4-chloro-2,6-dimethylheptane                                                              Cl   i-C.sub.4 H.sub.9                                                                  i-C.sub.4 H.sub.9                                                                       83.5%                          XXXII 2-t-butylazo-2-chloro-4-methyl-4-methoxypentane                                                        Cl   CH.sub.3                                                                            ##STR87##                                                                              54.5%                          XXXIII                                                                               1-t-butylazo-1-chloro-1-phenylethane                                                                   Cl   CH.sub.3                                                                           C.sub.6 H.sub.5                                                                         76.0%                          XXXIV 2-t-butylazo-2-chloro-4,4-dimethylpentane                                                              Cl   CH.sub.3                                                                            ##STR88##                                                                              64.5%                          XXXV  1-t-butylazo-1-methoxycyclohexane                                                                      OCH.sub.3                                                                           (CH.sub.2).sub.5                                                                            63.0%                          XXXVI 2-t-butylazo-2-methoxy-4-methylpentane                                                                 OCH.sub.3                                                                           CH.sub.3                                                                           i-C.sub.4 H.sub.9                                                                       48.0%                          XXXVII                                                                               4-t-butylazo-4-methoxy-2,6-dimethylheptane                                                             OCH.sub.3                                                                           i-C.sub.4 H.sub.9                                                                  i-C.sub.4 H.sub.9                                                                       76.0%                          XXXVIII                                                                              2-t-butylazo-4-methyl-2,4-dimethoxypentane                                                             OCH.sub.3                                                                           CH.sub. 3                                                                           ##STR89##                                                                              67.0%                          XXXIX 1-t-butylazo-1-methoxy-1-phenylethane                                                                  OCH.sub.3                                                                           CH.sub.3                                                                           C.sub.6 H.sub.5                                                                         88.0%                          XL    2-t-butylazo-2-methoxy-4,4-dimethylpentane                                                             OCH.sub.3                                                                           CH.sub.3                                                                           CH.sub.2 C(CH.sub.3).sub.3                                                              80.0%                          XLI   1-t-butylazo-1-azidocyclohexane                                                                        N.sub.3                                                                             (CH.sub.2).sub.5                                                                            83.0%                          XLII  2-t-butylazo-2-azido-4-methylpentane                                                                   N.sub.3                                                                             CH.sub.3                                                                           i-C.sub.4 H.sub.9                                                                       83.0%                          XLIII 4-t-butylazo-4-azido-2,6-dimethylheptane                                                               N.sub.3                                                                             i-C.sub.4 H.sub.9                                                                  i-C.sub.4 H.sub.9                                                                       86.0%                          XLIV  2-t-butylazo-2-azido-4-methyl-4-methoxypentane                                                         N.sub.3                                                                             CH.sub.3                                                                            ##STR90##                                                                              61.0%                          XLV   1-t-butylazo-1-azido-1-phenylethane                                                                    N.sub.3                                                                             CH.sub.3                                                                           C.sub.6 H.sub.5                                                                         96.0%                          XLVI  2-t-butylazo-2-t-butylperoxy-4-methylpentane                                                           OOt-Bu                                                                              CH.sub.3                                                                           i-C.sub.4 H.sub.9                                                                       75.0%                          XLVII 2-t-butylazo-2-t-butylperoxy-4-methyl-4-methoxy- pentane                                               OOt-Bu                                                                              CH.sub.3                                                                            ##STR91##                                                                              55.0%                          XLVIII                                                                               2-t-butylazo-2-t-butylperoxy-4,4-dimethylpentane                                                       OOt-Bu                                                                              CH.sub.3                                                                            ##STR92##                                                                              77.0%                          XLIX  1-t-butylazo-1-t-butylperoxy-cyclohexane                                                               OOt-Bu                                                                              (CH.sub.2).sub.5                                                                            65.0%                          L     1-t-butylazo-1-t-butylperoxy-1-phenylethane                                                            OOt-Bu                                                                              CH.sub.3                                                                           C.sub.6 H.sub.5                                                                         60.0%                          __________________________________________________________________________

EXAMPLE LI

Preparation of 2-t-Butylazo-2-thiocyanato-4-methylpentane ##STR93##

To a solution of .066 moles of sodium thiocyanate in 40 ml of 95% aqueous methanol, cooled to 5° C in an ice bath was added .05 m of the t-butylazo-α-chloro compound of Example XXX over 5-10 minutes. The reaction mixture was stirred an additional one-half hour and poured into 400 ml water. The organic layer was extracted with 50 ml pentane, the pentane solution dried over anhydrous Na₂ SO₄, filtered and the pentane evaporated. An infrared spectrum of the residue was in agreement with that of the desired product. Yield was 68%.

EXAMPLE LII

Preparation of 4-t-Butylazo-4-bromo-2,6-dimethylhepthane ##STR94##

To a solution of 0.02 moles of the t-butylhydrazone of diisobutyl ketone in 25 ml pentane, cooled to 5° C in an ice bath, was added 0.02 moles of bromine over 5 minutes. The reaction mixture was stirred an additional one-half hour at 5° C and then filtered to remove any insoluble impurities. The pentane filtrate was dried over anhydrous Na₂ SO₄, filtered and the pentane evaporated. An infrared spectrum of the residue was in agreement with that of the desired product. Yield was 40%.

EXAMPLE LIII

Preparation of 2-t-Butylazo-2-cyanato-4-methylpentane ##STR95##

To a solution of 4.86 g (.06 m) of potassium cyanate in 40 ml of 75% aqueous methanol, cooled to 5° C in an ice bath, was added 0.034 moles of the t-butylazo-α-chloro compound of Example XXX. After the addition was complete the reaction was stirred for an additional one half hour, poured into 400 ml water and the organic layer extracted with methylene chloride. The methylene chloride solution was dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated. An infrared spectrum of the residue was in agreement with that of the desired product. Yield was 74%.

EXAMPLE LIV

Preparation of 2-t-Butylazo-2-t-butoxy-4-methylpentane ##STR96##

To a slurry of .025 moles of potassium t-butoxide in 50 ml of anhydrous t-butanol was added 0.02 moles of the t-butylazo-α-chloro compound of Example XXX. The temperature was held at 28° C throughout the addition. After the addition was complete, the reaction was stirred for 20 minutes at 28° C and poured into 200 ml water. The organic layer was extracted with pentane, the pentane solution washed twice with water, dried over anhydrous sodium sulfate, filtered and the pentane evaporated. An infrared spectrum of the residue was in agreement with that of the desired product. Yield was 68%.

EXAMPLE LV

Preparation of 2-t-Butylazo-2-propylthio-4-methylpentane ##STR97##

To a solution of .04 m of propylmercaptan and 0.05 m of NaOH in 30 ml of 80% aqueous ethanol was added over 20 minutes at 10° C, .02 moles of the t-butylazo-α-chloro compound of Example XXX. When the addition was complete the reaction was stirred for one-half hour, poured into 200 ml water and the organic layer extracted with pentane. After washing with water, the pentane solution was dried over anhydrous Na₂ SO₄, filtered and the pentane evaporated. An infrared spectrum of the residue was in agreement with that of the desired product. Yield was 95%.

EXAMPLE LVI

Preparation of 2-(t-butylazo)-2-(benzoylperoxy)-4-methylpentane ##STR98##

To a solution of 1.0 g (.025 m) sodium hydroxide in 20 ml methanol, cooled to 5° C in an ice bath, was added a slurry of 4.2 g (0.0275 m) of 90% perbenzoic acid. A very viscous slurry resulted. To this slurry was added 4.1 g of 2-t-butylazo-α-choloro-4-methylpentane keeping the temperature below 10° C. After the addition was complete, the reaction was stirred an additional 45 minutes and then poured into 150 ml of ice water. A small amount of solid formed and was removed by filtration. The product was extracted from the water with 30 ml pentane and the pentane solution washed with 10% KOH and then water until the washings were neutral. The pentane solution was dried over anhydrous Na₂ SO₄, filtered and the pentane evaporated off leaving 4.1 g of a light yellow liquid. An infrared spectrum of the residue was in agreement with that of the desired product. The yield was 67%.

EXAMPLE LVII

Preparation of N,N'-Ethylene Bis(t-butylazoformamide) ##STR99##

To a solution of 8 g (.046 m) of isopropyl t-butylazocarboxylate in 25 ml ethanol, cooled to 5° C, was added 1.38 g (.023 m) of ethylenediamine dropwise over 5 minutes. The temperature slowly rose to 12° and then subsided. The reaction was stirred an addition 1/2 hour and the ethanol stripped off. The resulting solid was slurried in warm benzene and filtered. The filter cake weighed 1.7 g and had a melting point of 166°-167° C. The infrared spectrum of the yellow solid was in agreement with that of the title product.

Evaporation of the benzene from the filtrate left 2.3 g of a yellow liquid whose infrared spectrum was in agreement with the structure of the mono product t-butylazo-N-(2-aminoethyl) formamide.

EXAMPLE LVIII

Preparation of Di[1-(t-butylazo)-1,3-dimethylbutyl] Peroxide ##STR100##

To a solution of 1.18 g. (.0150 moles) of sodium peroxide in 30 ml. of 75% methanol cooled to 5° C. in a 50 ml. erlenmeyer flask was added 6.15 g. (.03 moles) of 2-t-butylazo-2-chloro-4-methylpentane over 10 minutes. The reaction was stirred an additional 45 minutes and poured into 200 ml. of ice water. The organic layer was extracted with pentane, washed twice with 50 ml. saturated ammonium sulfate, once with 50 ml. water, saturated sodium bicarbonate solution and again with water. The pentane solution was dried with anhydrous sodium sulfate, filtered and stripped leaving 3.8 g. of a light yellow liquid (70% yield). The infrared spectrum was in agreement with that of the title compound. The product began to gas rapidly upon reaching room temperature.

EXAMPLE LIX

Preparation of 2-t-Butylazo-2-hydroxy-4-methylpentane ##STR101##

To a solution of 1.28 g. (.016 moles) of 50% sodium hydroxide in 20 ml. water at 5° C. was added 3.2 g. (.015 moles) of 2-t-butylazo-2-chloro-4-methylpentane dropwise over 10 minutes. The reaction was stirred an additional 41/2 hours at 5° C. and extracted with 50 ml. of pentane. The pentane solution was washed twice with water, dried over anhydrous sodium sulfate, filtered and stripped leaving 2.6 g. of a light yellow liquid (90% yield). The infrared spectrum was in agreement with that of the title compound.

EXAMPLE LX

Preparation of 2-t-Butylazo-2-(propylamino)-4-methylpentane ##STR102##

To a solution of 2.37 g. (.04 moles) of n-propyl amine in 25 ml. of benzene was added 4.1 g. (.02 moles) of 2-t-butylazo-2-chloro-4-methylpentane. The reaction was stirred an additional 71/2 hours at 5°-10° C. During this period there was a slow precipitation of n-propyl amine hydrochloride. The reaction was placed in the refrigerator overnight (15° C.). The next morning the n-propyl amine hydrochloride was filtered off and weighed (1.54 g. or 81% of theory). The filtrate was washed with cold water, dried over sodium sulfate, and the benzene removed at 10° C. on a rotating evaporator leaving 3.9 g. (86% yield) of a light yellow liquid which slowly evolves gas at room temperature. The infrared spectrum was in agreement with that of the title compound.

EXAMPLE LXI

Preparation of 4-t-Butylazo-2,4-dimethyloctane ##STR103##

To a clean, dry, nitrogen purged 50 ml. round bottom 3 neck flask was transferred 25 ml. (1.4 g. = .022 moles) of 9% butyllithium in a mixture of one-third pentane and two-thirds hexane by means of a hypodermic syringe. The flask and contents were cooled to 5° C. and a slow continuous passage of nitrogen was passed through the system. To the solution was added slowly 2.1 g. (.01025 moles) of 2-t-butylazo-2-chloro-4-methylpentane in 10 ml. pentane from a pressure equalizing dropping funnel. After the addition was complete the reaction was stirred an additional 1 hour at 5° C. and the excess butyllithium destroyed by the slow addition of wet ether. The reaction mixture was then poured into 100 ml. H₂ O and the organic layer separated. The organic layer was dried over sodium sulfate, filtered and the solvent removed on a rotating evaporator leaving 2.0 g. (93% yield) of a light yellow liquid. The infrared and ultraviolet spectra were in agreement with the structure of the title compound.

EXAMPLE LXII

Preparation of 2-t-Butylazo-2-phenyl-4-methylpentane ##STR104##

To a clean, dry 250 ml. round bottom 4 neck flask equipped with a magnetic stirrer, thermometer, condenser and addition funnel, which was being purged with nitrogen was added an ether solution containing 0.06 moles of phenyllithium. The solution was cooled to 5° C. and a solution of 10.25 g. (.05 moles) of 2-t-butylazo-2-chloro-4-methylpentane in 50 ml. ether was added dropwise over one-half hour. After the addition was complete, the reaction was warmed to 20° C. and stirred for one-half hour. The excess phenyllithium was destroyed with wet ether and the reaction mixture poured into 200 ml. water. The ether layer was separated, dried over anhydrous sodium sulfate, filtered and the ether removed on a rotating evaporator leaving 11.9 g. (96%) of a liquid. The infrared spectrum was in agreement with the structure of the title compound.

EXAMPLE LXIII

Preparation of 1-t-Butylazo-1-phenylcyclohexane ##STR105##

To a clean, dry 250 ml. round bottom 4 neck flask equipped with a magnetic stirrer, thermometer, condenser and addition funnel, which was being purged with nitrogen, was added an ether solution containing 0.06 moles of phenylmagnesium bromide. The solution was cooled to 5° C. and a solution of 8.7 g. (.043 moles) of 1-t-butylazo-1-chloro-cyclohexane in 50 ml. of ether was added dropwise over one-half hour. After the addition was complete, the reaction was stirred for 15 minutes at room temperature and the excess phenylmagnesium bromide destroyed by the addition of wet ether. The reaction mixture was poured into 200 ml. of cold water and the ether layer separated, washed with 5% HCl, saturated sodium bicarbonate solution, saturated sodium chloride solution, dried over anhydrous sodium sulfate, filtered and the ether removed on a rotating evaporator leaving 9.75 g. (93%) of a yellow liquid. The infrared spectrum of the product was in agreement with the structure of the title compound.

EXAMPLE LXIV

Preparation of 2-Phenyl-4-[1-(t-butylazo)-1,3-dimethylbutyl]-Δ² -1,3,4-oxadiazolin-5-one ##STR106##

To a solution of 2.8 g. (0.026 moles) of 50% sodium hydroxide and 4.22 g. (0.026 moles) of 2-phenyl-Δ² -1,3,4-oxadiazolin-5-one in 30 ml. of methanol at 5° C. was added 5.14 g. (0.025 moles) of 2-t-butylazo-2-chloro-4-methylpentane dropwise over 10 minutes. After the addition was complete the reaction was stirred for an additional hour and poured into 200 ml. of water. The product was extracted with 50 ml. pentane, dried over anhydrous sodium sulfate, filtered, and the pentane removed on a rotating evaporator leaving 6.0 g. (73% yield) of dark yellow viscous liquid. The infrared spectrum of the product was in agreement with the structure of the title compound. Upon cooling the product crystallized and the material was pruified by crystallizing it out of pentane at -30° C. The white crystals melt at 40° C.

EXAMPLE LXV

Preparation of 2,2,5,8,8,11,11,14,17,17-decamethyl-5,14-diisobutyl-Δ³,15 -3,4,15,16-tetraaza-6,7,12,13-tetraoxaoctadecadiene ##STR107##

To a solution of 3.36 g. (.042 moles) of 50% sodium hydroxide and 3.92 g. (.022 moles) 2,5-dimethyl-2,5-dihydroperoxyhexane in 50 ml. of methanol at 5° C. was added 8.2 g. (.04 moles) of 2-t-butylazo-2-chloro-4-methylpentane dropwise over 10 minutes. After the addition was complete, the reaction was stirred for 1 hour at 5°-10° C. and poured into 250 ml. ice water. The product was extracted with 50 ml. pentane, washed with cold 10% KOH, water, saturated sodium bicarbonate solution, water, dried over anhydrous sodium sulfate, filtered and the pentane removed at 10° C. on the rotating evaporator leaving 8.3 g. (80% yield) of a light yellow liquid which evolves nitrogen at 30° C. The infrared spectrum of the product is in agreement with the structure of the title compound.

EXAMPLE LXVI

Preparation of Diethyl α-[1-(t-butylazo)-1,3-dimethyl-butyl]malonate ##STR108##

To a solution of .04 moles of sodium methoxide in 50 ml. methanol was slowly added 6.4 g. (.04 moles) diethyl malonate and the reaction stirred 1 hour and cooled to 5° C. To the cooled solution was added 8.2 g. (.04 moles) of 2-t-butylazo-2-chloro-4-methylpentane dropwise over 10 minutes. After the addition was complete, the reaction was stirred for an additional one-half hour and poured into 300 ml. cold water. The product was extracted with 100 ml. pentane, dried over anhydrous sodium sulfate, filtered and the pentane removed on a rotating evaporator leaving 9.8 g. (75% yield) of a yellow liquid. The infrared spectrum was in agreement with the structure of the title compound.

EXAMPLE LXVII

Reaction of the Sodium Salt of 2,4-Pentanedione with 2-t-Butylazo-2-chloro-4-methylpentane ##STR109##

To a solution of .03 moles of sodium methoxide in 40 ml. of methanol was added 3.6 g. (.03 moles) of 2,4-pentanedione and the reaction stirred one-half hour and cooled to 5° C. To the cooled solution was added 6.15 g. (.03 moles) of 2-t-butylazo-2-chloro-4-methylpentane dropwise over 10 minutes. After the addition was complete, the reaction was stirred an additional 1 hour and poured into 250 ml. of cold water. The product was extracted with pentane, dried over anhydrous sodium sulfate, filtered and the pentane removed on a rotating evaporator leaving 6.9 g. (86% yield) of a yellow liquid. The infrared spectrum of the product indicated that the product was a mixture of the above two isomeric structures.

EXAMPLE LXVIII

Preparation of 2-t-Butylazo-2-phenylhydrazo-4-methylpentane ##STR110##

To a solution of 2.17 g. (.02 moles) of phenylhydrazine in 25 ml. benzene, cooled to 5° C., was added 2.05 g. (0.1 mole) of 2-t-butylazo-2-chloro-4-methylpentane dropwise. After the addition was complete the reaction was stirred for 3 hours at 5°-10° C. and then placed in the refrigerator overnight (15° C.). The next morning the phenylhydrazine hydrochloride which had formed was filtered off, the benzene filtrate washed with water, dried over anhydrous sodium sulfate, filtered and the benzene removed on a rotating evaporator at 10° C. The product brownish-yellow liquid decomposes rapidly at room temperature. The infrared spectrum of the product was in agreement with the structure of the title compound.

EXAMPLE LXIX

Preparation of 2-t-Butylazo-2-t-butylhydrazo-4-methylpentane ##STR111##

To a solution of 2.15 g. (.02 moles) of 82% t-butylhydrazine in 25 ml. of benzene was added 2.05 g. (.01 mole) of 2-t-butylazo-2-chloro-4-methylpentane holding the temperature at 5°-10° C. with an ice bath. The reaction was stirred an additional 3 hours and stored in the refrigerator (15° C.) overnight. The next morning the insoluble t-butyl-hydrazine hydrochloride which had formed was filtered off (1.0 g. or 84% of theory). The benzene filtrate was washed with water, dried over anhydrous sodium sulfate, filtered and the benzene removed at 10° C. on a rotating evaporator leaving 2.4 g. (94.5%) of a yellow liquid. The product evolves nitrogen at room temperature. The infrared spectrum of the product is in agreement with the structure of the title compound.

EXAMPLE LXX

Reaction of the Sodium Salt of 2-Nitroethane with 2-Butylazo-2-chloro-4-methylpentane ##STR112##

To a solution of .03 moles of sodium methoxide in 30 ml. of methanol was added dropwise 2.25 g. (.03 moles) of nitroethane. The sodium salt which formed was insoluble in the methanol. The methanol slurry was cooled to 5° C. and 6.15 g. (.03 moles) of 2-t-butylazo-2-chloro-4-methylpentane was slowly added to it holding the temperature at 5° C. with an ice bath. After the addition was complete, the reaction was stirred an additional hour at 5° C. and poured into 200 ml. of water. The organic layer was extracted with 50 ml. of pentane, dried over anhydrous sodium sulfate, filtered and the pentane removed on a rotating evaporator leaving 6.4 g. (87.6%) of a light yellow liquid which evolves nitrogen at room temperature. The infrared spectrum of the product indicated that the product was a mixture of the above two isomeric structures.

EXAMPLE LXXI

Preparation of 2-t-Butylazo-2-(t-butylperoxycarbonyloxy)butane ##STR113##

Potassium t-butylperoxy carbonate was prepared in 67% yield by adding anhydrous t-butylhydroperoxide to a solution of potassium t-butoxide in t-butanol and then carbonating the resultant solution.

To a stirred slurry of 18.9 grams (0.11 mole) potassium t-butylperoxy carbonate in 80 ml of N, N-dimethylformamide in a 250 ml round bottom flask was slowly added 17.66 grams (0.1 mole)2-t-butylazo-2-chlorobutane. After the addition was complete the reaction was stirred for 5 hours at room temperature and poured into 350 ml water. The product was taken up in 100 ml pentane and the pentane solution washed with 5% HCl, water and saturated sodium bicarbonate solution. The pentane solution was dried over sodium sulfate, filtered and the pentane evaporated under reduced pressure. The residue weighed 22.9 grams (83% yield) and its infrared spectrum was in agreement with the structure of 2-t-butylazo-2-(t-butyl-peroxycarbonyloxy)butane (strong carbonyl band at 1750 cm⁻ ¹).

EXAMPLE LXXII

Preparation of 2-t-Butylazo-2-hydroxypropane ##STR114## Method A

Into a 3 liter jacketed reactor was added 500 ml t-butyl alcohol, 500 ml water and 192 grams (2.4 moles) of 50% sodium hydroxide. The solution was cooled to 15° C by circulating ice water through the jacket. With rapid stirring 325 grams of 2-t-butylazo-2-chloropropane was slowly added from a dropping funnel over 20 minutes while holding the temperature at 15°-20° C. The reaction was stirred an additional 15 minutes at 15° C, the reaction temperature lowered to 5°-10° C and the reaction stirred an additional hour. At the end of the stirring period the lower aqueous layer was separated. The organic layer was washed 4 times with 5% sodium bicarbonate solution to remove the t-butyl alcohol. There was still t-butyl alchohol present in the organic layer so 300 ml pentane was added and the organic layer washed 2 more times with 5% sodium bicarbonate. The organic layer was dried over anhydrous sodium sulfate, filtered and the pentane evaporated on a rotating evaporator at 10° C. The product was a yellow liquid weighing 171 grams (60% crude yield). The infrared spectrum was in agreement with the structure of 2-t-butylazo-2-hydroxypropane.

Followig this procedure, 1-t-butylazo-1-hydroxycyclohexane (88% crude yield), 1-t-amylazo-1-hydroxycyclohexane (94% crude yield) and 2-t-amylazo-2-hydroxybutane (82% crude yield) were prepared from the corresponding α-chloroazo.

Method B

To a jacketed 3 liter reactor equipped with a mechanical stirrer, thermometer, condenser and dropping funnel was added 256.2 grams (2.0 moles) of acetone t-butylhydrazone. With rapid agitation and ice water circulated through the reactor jacket, approximately 1330 mls (about 2 moles) of commercial sodium hypochlorite (11.2% NaClO by weight) was added dropwise over 2 hours while holding the temperature at 10° C ± 2° C. The reaction was more exothermic at the beginning of the addition and consequently the NaClO addition was slower at the beginning and was increased as the addition went along. The extent of reaction was followed by vapor phase chromatography and the reaction was complete 5 minutes after the addition was complete. The aqueous phase was separated and the organic phase cooled to 5° C and washed with 400 ml of 15% aqueous sodium bisulfite solution, 400 ml of saturated sodium bicarbonate solution, dried over anhydrous sodium sulfate, filtered and weighed. The crude yield was 241.2 grams (83.6 % crude % yield) of a yellow liquid. The product was stored in a vented poly bottle in a freezer. The infrared spectrum of the product was similar to that obtained in Method A.

Following this procedure, the following α-hydroxyazos were prepared from hydrazones ("C.Y." = crude yield and "t-BH" = t-butylhydrazone): 2-t-butylazo-2-hydroxybutane (87.9% C.Y. from methyl ethyl ketone t-BH), 2-t-butylazo-2-hydroxypentane (87.5% C.Y. from 2-pentanone t-BH), 2-t-butylazo-2-hydroxyhexane (82% C.Y. from 2-hexanone t-BH), 2-t-butylazo-2-hydroxyheptane (64.4% C.Y. from 2-heptanone t-BH), 3-t-butylazo-3-hydroxyheptane (75.7% C.Y. from 3-heptanone t-BH), 2-t-butylazo-2-hydroxyoctane (87% C.Y. from 2-octanone t-BH), and 2-t-amylazo-2-hydroxypropane (76% C.Y. from acetone t-amylhydrazone).

Example LXIII

Preparation of n-Butyl 4-t-Butylazo-4-hydroxyvalerate ##STR115##

n-Butyl levulinate t-butylhydrazone was prepared by refluxing an aqueous solution of t-butylhydrazine and an equivalent amount of n-butyl levulinate for approximately one hour. The organic layer that formed was separated, dried over anhydrous sodium sulfate and filtered. Then 40 grams (0.165 mole) of the n-butyl levulinate t-butylhydrazone was dissolved in 50 ml pentane and transferred to a 250 ml jacketed reactor equipped with a mechanical stirrer, thermometer, condenser and oxygen inlet tube. The solution was warmed to 35° C and with rapid stirring the oxygen was slowly bubbled into the solution. The reaction was monitored by following the disappearance of the n-butyl levulinate t-butylhydrazone by vapor phase chromatography. After the oxidation of the t-butylhydrazone was 50% complete, the reaction temperature was lowered to 20° C and held there for the remainder of the oxidation.

After the oxidation was complete, the temperature of the pentane solution of the n-butyl 4-t-butylazo-4-hydroperoxyvalerate was lowered to 5° C and with rapid stirring 5% aqueous sodium sulfite solution was added in 100 ml increments while holding the temperature below 15° C. The reaction was monitored by following the exotherm generated upon addition of the sulfite solution. When there was no exotherm generated upon addition of the sulfite solution, the reduction was considered complete. This required approximately 1,200 ml of the 5% sodium sulfite solution. The pentane solution was washed with 10% aqueous sodium bicarbonate solution, dried over anhydrous sodium sulfate, filtered and the pentane stripped off on a rotating evaporator at 10° C. The product weighed 42.6 grams (94% crude yield) and its infrared spectrum was in agreement with the structure of n-butyl 4-t-butylazo-4-hydroxyvalerate.

Example LXXIV

Polymerization of Styrene with 2-t-Butylazo-2-hydroxypropane

An 18 × 150 mm pyrex test tube was filled with 10.0 grams of distilled styrene monomer and 0.121 grams (8.4 × 10.sup.⁻⁴ moles) of 2-t-butylazo-2-hydroxypropane. The test tube was flushed out with nitrogen and placed in a constant temperature bath thermostatted at 70° C. After 4.0 hours at 70° C, the tube was removed and quickly chilled to -20° F to prevent post polymerization. The sealed tube was then broken and the polymer dissolved in 1000 ml of methanol to precipitate the polystyrene. The polymer was separated by filtration and dried in an oven at 50°-55° C. The dry polymer weighed 3.4 grams (34% conversion). The rate of conversion of monomer to polymer was 8.5% per hour.

Example LXXV

Polymerization of Styrene with 2-t-Butylazo-2-hydroxybutane

An 18 × 150 mm pyrex test tube was filled with 10.0 grams of distilled styrene monomer and 0.134 grams (8.5 × 10.sup.⁻⁴ moles) of 2-t-butylazo-2-hydroxybutane from Example V. The test tube was flushed out with nitrogen and placed in a constant temperature thermostatted bath at 70° C. After 6.0 hours at 70° C, the tube was removed and quickly chilled to -20° F to prevent post polymerization. The sealed tube was then broken and the polymer dissolved in 1000 ml of methanol to precipitate the polystyrene. The polymer was separated by filtration and dried in an oven at 50°-55° C. The dry polymer weighed 4.8 grams (48% conversion). The rate of conversion of monomer to polymer was 8.0% per hour.

Example LXXVI

The following α-carbonato azos were prepared by reacting 0.11 mole of the appropriate metal alkyl carbonate with 0.1 mole of the appropriate α-chloroazo in N,N-dimethylformamide at 45° C. The reactions were generally complete in 5 hours and the products were isolated by diluting the reaction mixture with water and extracting with pentane.

    __________________________________________________________________________                                  Starting  %                                       Product         metal alkyl carbonate                                                                       α-chloroazo                                                                        Yield                                   __________________________________________________________________________     2-t-butylazo-2-(ethoxy-                                                                        sodium ethyl carbonate                                                                      2-t-butylazo-2-                                                                          78%                                     carbonyloxy)butane           chlorobutane                                      2-t-butylazo-2-(isopropoxy-                                                                    sodium isopropyl                                                                            2-t-butylazo-2-                                                                          86%                                     carbonyloxy)butane                                                                             carbonate    chlorobutane                                      2-t-butylazo-2-(t-butoxy-                                                                      potassium t-butyl                                                                           2-t-butylazo-2-                                                                          52%                                     carbonyloxy)butane                                                                             carbonate    chlorobutane                                      2-t-butylazo-2-(methoxy-                                                                       sodium methyl carbonate                                                                     2-t-butylazo-2-                                                                          74%                                     carbonyloxy)butane           chlorobutane                                      2-t-butylazo-2-(methoxy-                                                                       sodium methyl carbonate                                                                     2-t-butylazo-2-                                                                          58%                                     carbonyloxy)propane          chloropropane                                     2-t-butylazo-2-(methoxy-                                                                       sodium methyl carbonate                                                                     2-t-butylazo-2-                                                                          70%                                     carbonyloxy)-4-methyl-       chloro-4-                                         pentane                      methylpentane                                     1-t-butylazo-1-(methoxy-                                                                       sodium methyl carbonate                                                                     1-t-butylazo-                                                                            74%                                     carbonyloxy) cyclohexane     1-chlorocyclo-                                                                 hexane                                            __________________________________________________________________________

Example LXXVII

Preparation of 2-t-Butylazo-2-chloropropane ##STR116##

Into a solution of 25.6 g (0.2 m) of acetone t-butylhydrazone in 150 ml of pentane cooled to -35° C in a 250 ml 4-neck round bottom flask equipped with a mechanical stirrer, thermometer and a chlorine inlet and outlet, was passed chlorine until the reaction no longer absorbed any more chlorine. There was an increase in weight of approximately 7.1 g. When the chlorine absorption ceased, the chlorine addition was stopped and the reaction mixture was allowed to slowly warm up to 0° C. It was then poured into 200 ml of water to dissolve the acetone t-butylhydrazone hydrochloride. The pentane layer was separated, washed with water, saturated 10% NaHCO₃ solution, dried, filtered and stripped. The product weighed 15.8 g (48.6 % yield).

Following this procedure, the following α-chloroazos were likewise prepared ("t-BH" is t-butylhydrazone and "t-CH" is t-cumylhydrazone): 2-t-butylazo-2-chlorooctane (in 45.3% crude yield from 2-octanone t-BH), n-butyl 4-t-butylazo-4-chlorovalerate (in 61% crude yield from n-butyl levulinate t-BH), 2-t-cumylazo-2-chloropropane (in 49% crude yield from acetone t-CH prepared by refluxing acetone and an aqueous solution of t-cumylhydrazine, the hydrazine being prepared according to the method of C. G. Overberger et al, J. Am. Chem. Soc. 80, 6562 (1958)), 2-t-cumylazo-2-chloro-4-methylpentane (in 50% crude yield from methyl isobutyl ketone t-CH prepared from methyl isobutyl ketone and t-cumylhydrazine), and ethyl 3-t-butylazo-3-chlorobutirate (in 33.6% crude yield from ethyl acetoacetate t-BH prepared from t-butylhydrazine and ethyl acetoacetate).

Example LXXVIII

Preparation of 1-t-Butylazo-1-chloro-2,4,4-trimethylcyclopentane ##STR117##

2,4,4-Trimethylcyclopentanone t-butylhydrazone was prepared by refluxing an aqueous solution of t-butylhydrazine with an equimolar amount of 2,4,4-trimethylcyclopentanone.

Into a solution of 45.5 grams (.232 mole) of 2,4,4-trimethylcyclopentanone t-butylhydrazone and 25.5 grams (.232 mole) of triethylamine in 250 ml pentane, cooled to -20° C in a 500 ml 4-neck round bottom flask equipped with a mechanical stirrer, thermometer, chlorine inlet and outlet, was passed 16.5 grams (.232 mole) of chlorine over 25 minutes. After the addition was complete, the reaction was slowly warmed to 0° C and filtered to remove the triethylamine hydrochloride. The filtrate was dried over anhydrous sodium sulfate, filtered and the pentane evaporated under reduced pressure leaving 50.0 grams (93.7% crude yield) of a yellow liquid whose infrared spectrum was in agreement with the structure of 1-t-butylazo-1-chloro-2,4,4-trimethylcyclopentane.

Example LXXIX

Preparation of 3-t-Butylazo-3-chloro-2,2,4,4-tetramethylcyclobutanone ##STR118##

2,2,4,4-Tetramethylcyclobutan-1,3-dione mono-t-butylhydrazone was prepared by refluxing an aqueous solution of t-butylhydrazine with an equimolar amount of 2,2,4,4-tetramethylcyclobutan-1,3-dione.

Into a solution of 21.0 grams (0.1 mole) of 2,2,4,4-tetramethylcyclobutan-1,3-dione mono-t-butylhydrazone and 10.1 grams (0.1 mole) of triethylamine in 150 ml of methylene chloride, cooled to -20° C in 250 ml 4-neck round bottom flask equipped with a mechanical stirrer, thermometer, chlorine inlet and outlet, was passed 7.1 grams (0.1 mole) of chlorine over 20 minutes. After the addition was complete, the reaction was warmed to -5° C over 15 minutes and filtered. The filtrate was dried over anhydrous sodium sulfate, filtered and the methylene chloride evaporated under reduced pressure. The residue was a mixture of triethylamine hydrochloride and a yellow liquid. Pentane was added to the residue and the slurry filtered to remove the triethylamine hydrochloride which had been soluble in the methylene chloride. The pentane was evaporated from the filtrate under reduced pressure leaving 22.1 grams (90.5% crude yield) of a yellow liquid whose infrared spectrum was in agreement with the structure of 3-t-butylazo-3-chloro-2,2,4,4-tetramethylcyclobutanone.

Example LXXX

General Preparation of other α-Chloroazoalkanes

The α-chloroazoalkanes found in Table LXXX were prepared by passing an essentially equimolar amount of chlorine into a pentane solution of equimolar amounts of the corresponding t-alkylhydrazone and triethylamine at 0°-5° C and filtering off the triethylamine hydrochloride that formed. The pentane filtrate was dried over anhydrous sodium sulfate, filtered and the pentane evaporated under reduced pressure. The infrared spectra of the products were in agreement with the structures of the desired products in all cases.

                                      TABLE LXXX                                   __________________________________________________________________________     Preparation of t-Alkyl-α-chloroazoakanes                                                                                        Yield of                Name of Compound            Starting t-Alkylhydrazone  α-Chloroazo       __________________________________________________________________________     n-butyl 4-t-amylazo-4-chlorovalerate                                                                       n-butyl levulinate t-amylhydrazone                                                                        99%                     4-t-butylazo-4-chloropentyl acetate                                                                        5-acetoxy-2-pentanone t-butylhydrazone                                                                    68.5%                   methyl 4-t-butylazo-4-chlorovalerate                                                                       methyl levulinate t-butylhydrazone                                                                        91%                     2-t-butylazo-2-chloroundecane                                                                              2-undecanone t-butylhydrazone                                                                             92%                     7-t-butylazo-7-chlorotridecane                                                                             di -n-hexyl ketone t-butylhydrazone                                                                       92%                     1-t-butylazo-1-chloro-1-(norborn-2-en-5yl)ethane                                                           methyl norborn-2-en-5-yl ketone                                                t-butylhydrazone           73.5%                   1-t-butylazo-1-chloro-1-(norborn-2-yl)ethane                                                               methyl norborn-2-yl ketone t-butylhydrazone                                                               77%                     5-t-butylazo-5-chlorohexene allylacetone t-butylhydrazone                                                                             89%                     1-t-butylazo-1-chlorododecane                                                                              cyclododecanone t-butylhydrazone                                                                          95%                     2-t-butylazo-8-chloro-tricyclo [5.2.1.0.sup.2,6 ]decane                                                    8-ketotricyclo [5.2.1.0.sup.2,6 ]decane                                        t-butylhydrazone           91.5%                   1-t-butylazo-1-chloro-2-carbethoxycyclopentane                                                             2-carbethoxycyclopentanone t-butylhydrazone                                                               77.5%                   1-t-butylazo-1-cyclopropyl-1-chloroethane                                                                  cyclopropyl methyl ketone t-butylhydrazone                                                                85.5%                   2-t-butylazo-2-chloro-1-phenylpropane                                                                      phenyl-2-propanone t-butylhydrazone                                                                       92.5%                   3-t-butylazo-3-chloro-1-phenylbutane                                                                       benzylacetone t-butylhydrazone                                                                            91%                     1-t-butylazo-1-chlorocyclooctane                                                                           cyclooctanone t-butylhydrazone                                                                            82%                     3-t-butylazo-3-chloropentane                                                                               3-pentanone t-butylhydrazone                                                                              87%                     allyl 4-t-butylazo-4-chlorovalerate                                                                        allyl levulinate t-butylhydrazone                                                                         87%                     2-t-butylazo-2-chlorohexane 2-hexanone t-butylhydrazone                                                                               90%                     2-t-butylazo-2-chloro-5-methyloctane                                                                       5-methyl-2-octanone t-butylhydrazone                                                                      90%                     n-butyl 4-t-cumylazo-4-chlorovalerate                                                                      n-butyl levulinate t-cumylhydrazone                                                                       95%                     2-t-amylazo-2-chloro-4-methylpentane                                                                       methyl isobutyl ketone t-amylhydrazone                                                                    87%                     2-t-butylazo-2-chlorobutane methyl ethyl ketone t-butylhydrazone                                                                      90%                     2-t-amylazo-2-chlorobutane  methyl ethyl ketone t-amylhydrazone                                                                       78.5%                   1-t-amylazo-1-chlorocyclohexane                                                                            cyclohexanone t-amylhydrazone                                                                             97.5%                   1-t-butylazo-1-chlorocyclopentane                                                                          cyclopentanone t-butylhydrazone                                                                           86%                     __________________________________________________________________________

Example LXXXI

Preparation of 2-t-Butylazo-2-bromopropane ##STR119##

Into a solution of 25.6 grams (0.2 mole) of acetone t-butylhydrazone and 20.3 grams (0.2 mole) of triethylamine in 200 ml of pentane, cooled to 5° C in a 500 ml 4-neck round bottom flask equipped with a mechanical stirrer and thermometer, was added 31.9 grams (0.2 mole) of bromine from an addition funnel. After the addition was complete the reaction was stirred an additional one-half hour at 5° C, filtered to remove the triethylamine hydrobromide and the pentane evaporated from the filtrate under reduced pressure. The residue was an orange yellow liquid weighing 40 grams (96.6% crude yield). The infrared spectrum of the residue was in agreement with the structure of 2-t-butylazo-2-bromopropane.

Example LXXXII Low Conversion Polymerization of Styrene

A solution of styrene containing 5×10.sup.⁻⁴ moles per deciliter of the tert.-alkyl-α-substituted-azoalkane was heated in a constant temperature oil bath (the temperature of the bath depending on the thermal stability of the individual azo compounds) and the change in density, which is a measure of polymer formation, was followed by means of a dilatometer to measure polymerization rates (R_(p)) at 5% and 10% conversion to polystyrene. The rates obtained at 5% and 10% conversion are recorded in moles per liter per minute in Table LXXXII for the individual azo compounds. Their rate at 10% conversion (f₁) is divided by the rate of a standard (f₂) at the same temperature and concentration to give an efficiency rating f₁ / f₂.

                                      Table LXXXII                                 __________________________________________________________________________     Exam. No.                                                                             Bath  R.sub.p (m/1/min)                                                                      at                                                        of Azo Temp. 5%      10%    f.sub.1 /f.sub.2                                                                    f.sub.2                                       __________________________________________________________________________     XXXVIII                                                                               115° C.                                                                       --      --     0.38 di-t-butyl                                                                     peroxide                                      XLI    100° C.                                                                       9.10×10.sup..sup.-3                                                              9.10×10.sup..sup.-3                                                             0.58 t-butyl per-                                                                   benzoate                                      XLIV    85° C.                                                                       7.28×10.sup..sup.-3                                                              6.89×10.sup..sup.-3                                                             1.19 benzoyl                                                                        peroxide                                      LXII    70° C.                                                                       5.42×10.sup..sup.-3                                                              4.48×10.sup..sup.-3                                                             1.41 benzoyl                                                                        peroxide                                      LXIII   85° C.                                                                       5.64×10.sup..sup.-3                                                              5.48×10.sup..sup.-3                                                             1.32 benzoyl                                                                        peroxide                                      __________________________________________________________________________

Example LXXXIII Curing of An Unsaturated Polyester-Styrene Resin with tert.-Alkyl-α-substituted-azoalkanes

The curing results for several of the azos of this invention are set forth in Table LXXXIII. The curing procedure and resin are described in Example III.

                                      Table LXXXII                                 __________________________________________________________________________     Example No.        Minutes to           Barcol                                 of Azo  Bath Temp. (° C.)                                                                  Peak Exotherm                                                                           Peak Exotherm (° F)                                                                 Hardness                               __________________________________________________________________________     XXXV    145        5.7      396         40                                     XXXVI   115        7.2      400         40                                     XXXIX    82        6.6      371         40                                     XLII    100        5.3      418         40                                     LI      115        3.4      438         45                                     LIII    115        3.8      412         45                                     LIV     115        2.8      358         20                                     LXI     130        11.1     382         40                                     LXIII   100        4.8      435         35                                     LXIX     82        1.4      275         40                                     __________________________________________________________________________ 

What is claimed is:
 1. A compound of the formula (R")₃ C--N=N--R' in which (R")₃ C-- is different from -R' and wherein:a. R' is --C(R₁) (R₂) (Z) or ##STR120## b. R" is alkyl of 1-13 carbons, phenalkyl of 7-12 carbons or phenyl, not more than one R" being phenyl; c. R₁ and R₂ are alkyl of 1-13 carbons, phenalkyl of 7-12 carbons, cycloalkyl of 3-12 carbons or, taken together, alkylene of 2-16 carbons, and R₂ can also be phenyl; d. R₃ and R₄ are hydrogen, alkyl of 1-13 carbons, cycloalkyl of 3-12 carbons or, taken together, alkylene of 2-16 carbons; e. R₅ is alkyl of 1-13 carbons, cycloalkyl of 3-12 carbons or aryl of 6-14 carbons; f. R₆ is alkyl of 1-13 carbons; g. R₇ and R₈ are hydrogen or alkyl of 1-13 carbons; h. R₆ and R₇ together can form alkylene of 2-16 carbons; i. Z is --Cl, --Br, --OR₅, --N₃, --SCN, --OCN, --OH, --NHR₅, --R₅, --NHNHR₅, --OC(=O)OR₅, --OC(=O)OOR, ##STR121## j. R is (R")₃ C.
 2. A compound of the formula (R")₃ C--N=N--R' in which (R")₃ C-- is different from --R' and wherein:a. R' is --C(R₁) (R₂) (Z) or ##STR122## b. R" is alkyl of 1-13 carbons, phenyl, benzyl or phenethyl, not more than one R" being phenyl; c. R₁ and R₂ are alkyl of 1-13 carbons, cycloalkyl of 3-6 carbons or, taken together, alkylene of 2-16 carbons, and R₂ can also be phenyl; d. R₃ and R₄ are hydrogen, alkyl of 1-4 carbons, cycloalkyl of 3-6 carbons, or together can form alkylene of 2-16 carbons; e. R₅ is alkyl of 1-13 carbons, cycloalkyl of 3-6 carbons or phenyl; f. R₆ is alkyl of 1-13 carbons; g. R₇ and R₈ are hydrogen or alkyl of 1-13 carbons; h. R₆ and R₇ together can form alkylene of 2-16 carbons; and i. Z is --Cl, --Br, --OR₅, --N₃, --SCN, --OCN, --OH, --HNR₅, --R₅, --NHNHR₅, --OC(=O)H, --OC(=O)R₅, --0C(=O)OR₅, ##STR123##
 3. A compound as in claim 2 where R' is --C(R₁) (R₂)Z.
 4. A compound as in claim 3 where Z is --OH, --Cl or --OC(=O)OR₅.
 5. A compound as in claim 4 where (R")₃ C-- is t-butyl or t-amyl.
 6. A compound as in claim 3 where R" is alkyl and R₁ and R₂ are alkyl or join to form alkylene.
 7. A compound of claim 6, 1-t-butylazo-1-chlorocyclohexane.
 8. A compound of claim 6, 2-t-butylazo-2-chloro-4-methyl-4-methoxypentane.
 9. A compound of claim 6, 1-t-butylazo-1-methoxycyclohexane.
 10. A compound of claim 1, 2-t-butylazo-2-(t-butylperoxycarbonyloxy)butane.
 11. A compound of claim 6, 2-t-butylazo-4-methyl-2,4-dimethoxypentane.
 12. A compound of claim 6, 2-t-butylazo-2-azido-4-methylpentane.
 13. A compound of claim 6, 2-t-butylazo-2-hydroxy-4-methylpentane.
 14. A compound of claim 6, 2-t-butylazo-2-hydroxypropane.
 15. A compound of claim 6, 2-t-butylazo-2-hydroxybutane.
 16. A compound of claim 2, 4-t-butylazo-2, 4-dimethyloctane.
 17. A compound of claim 2, 2-t-butylazo-2-(methoxycarbonyloxy)-butane.
 18. A compound of claim 2, 1-t-butylazo-1-phenylcyclohexane.
 19. A compound of claim 6, 2-(t-butylazo)-2-chloro-4-methylpentane.
 20. A compound of claim 2, 1-(t-butylazo)-1-methoxy-1-phenylethane. 